フッ化チタン(IV)カリウムからの窒化チタンウイスカーの合成
スポンサーリンク
概要
- 論文の詳細を見る
Titanium nitride (TiN) whiskers was formed by heating of potassium Fluorotitanate (IV) (K_2TiF_6) above 1300℃ on the outer surface of graphite tube in a stream of nitrogen. It was assumed that one of the important process about the formation of TiN whisker and coating was the reaction of titanium fluorides and potassium fluoride, which were formed by thermal decomposing of potassium fluotitanate (III) , with alumina tube. The shape and microstructure of the whiskers were observed by SEM and TEM. The main cross-sections of whiskers were square and regular hexagon. It was suggested that the whiskers having a square cross-section grew by layer growth mechanism on {111} tip faces of whiskers in the axial direction and on {110} lateral faces of them in the radial direction, respectively.
- 社団法人日本セラミックス協会の論文
- 1990-01-01
著者
-
田渕 光春
立命館大学大学院理工学研究科
-
金子 泰成
立命館大学理工学部
-
岩崎 弘通
立命館大学理工学部化学科
-
金子 泰成
立命館大学 理工学部
-
岩崎 弘通
立命館大学 理工学部
-
田渕 光春
立命館大学
関連論文
- アルミナセラミックス組成物に於けるパラフィンワックスの影響 (セラミックスの射出成形)
- N-メチルピロリドンを用いた金属粉末射出成形体の抽出脱脂
- β-TCPを原料粉末に用いたセラミックスの射出成形
- 固相反応を利用した高純度の水酸アパタイト及び TCP の射出成形
- 滑剤の検討 (セラミックスの射出成形)
- S-50 C 粉末の射出成形
- アルミナの射出成形 : 脱脂機構の検討
- 金属粉末の射出成形 : バインダーの選択
- アルミナの射出成形
- 金属ケイ素の射出成形