多重モードワイブル分布を用いた窒化ケイ素の強度解析
スポンサーリンク
概要
- 論文の詳細を見る
A maximum likelihood method for estimating multimodal Weibull parameters from the data of strength and fracture origin for different types of specimens was studied. Three kinds of 4-point bending test and one kind of tensile test were carried out for Si_3N_4 ceramics and the fracture origin of each specimen was investigated. A set of multimodal Weibull parameters of the Si_3N_4 ceramics was estimated by the maximum likelihood method. In this method parameters can be determined so as to maximize the likelihood function which is the product of the individual likelihood functions of each type of specimen. The strength distributions calculated from those parameters were in good agreement with the experimental results. It is indicated that the probability of failure can be predicted by collecting the size effects for every kind of fracture origin. The probability of failure after eliminating a critical fracture origin was estimated for each type of specimen.
- 社団法人日本セラミックス協会の論文
- 1992-10-01
著者
関連論文
- 1532 多孔体組織のモデル化・定量化と圧力損失との関係
- ハステロイXRの900℃での定常および非定常多軸応力クリープ
- セラミックスの疲労(第3報) : 常圧焼結窒化ケイ素の高温繰り返し疲労挙動
- セラミックスの疲労(第2報) : 常圧焼結窒化ケイ素の室温における繰り返し疲労特性
- 常圧焼結窒化ケイ素の多軸応力下の破壊挙動
- セラミックスの疲労(第1報) : 引張-圧縮繰り返し応力下における常圧焼結窒化ケイ素の疲労挙動
- 静止部品用セラミック部材の開発経緯
- 多重モードワイブル分布を用いた窒化ケイ素の強度解析
- 常圧焼結窒化ケイ素の多軸応力下の破壊挙動(第2報)
- セラミックスの疲労(第4報) : 常圧焼結窒化ケイ素の引張応力下の静的疲労強度
- 多軸応力下のセラミックスの破壊強度 (エンジン用セラミックスの現状と将来展望--素材を材料として使いこなすために-1-)