The slow crack growth and creep characteristic of two sintered silicon nitride ceramics under tensile stress were studied. The static fatigue strength degraded with increasing temperature due to the slow crack growth and the creep deformation. In slow crack growth failure without creep deformation, the power law for crack growth rate controlled the strength degradation under constant stress and/or constant stress rate. The modified Larson-Miller parameter was applicable to life prediction under static stress in creep deformation regime. The static fatigue behavior was mainly dominated by the grain boundary nature at elevated temperature. Crystallized phases at grain boundary inhibit not only slow crack growth by stress corrosion cracking but also cavity formation during creep deformation.
- 社団法人日本セラミックス協会の論文
- 1990-01-01
著者
関連論文
- セラミックスの疲労(第3報) : 常圧焼結窒化ケイ素の高温繰り返し疲労挙動
- セラミックスの疲労(第2報) : 常圧焼結窒化ケイ素の室温における繰り返し疲労特性
- 常圧焼結窒化ケイ素の多軸応力下の破壊挙動
- セラミックスの疲労(第1報) : 引張-圧縮繰り返し応力下における常圧焼結窒化ケイ素の疲労挙動
- 多重モードワイブル分布を用いた窒化ケイ素の強度解析
- 常圧焼結窒化ケイ素の多軸応力下の破壊挙動(第2報)
- セラミックスの疲労(第4報) : 常圧焼結窒化ケイ素の引張応力下の静的疲労強度
- 多軸応力下のセラミックスの破壊強度 (エンジン用セラミックスの現状と将来展望--素材を材料として使いこなすために-1-)