SiC-Cプラズマ焼結体中のカーボン
スポンサーリンク
概要
- 論文の詳細を見る
Plasma sintered SiC- C composites were observed by transmission electron microscopy in order to investigate the existing state of carbon, interface structure between SiC and C, and grain; boundary structure in SiC. The present observation was helpful in discussing the sintering mechanism and in explaining the high hardness and high toughness of plasma sintered SiC- C composites. The results obtained are summarized as follows. (1) Graphite in plasma sintered SiC- C composites existed as (1) fine polycrystals, (2) fibrous crystals and (3) single crystals. The fine polycrystals and fibrous crystals had no orientation around a pore, but some orientation between SiC grains because of the compressive stress generated by the difference in the thermal expansion coefficient between SiC and graphite. Single crystals of graphite were observed at grain boundaries between SiC crystals. In the graphite, cracks were formed parallel to the basal plane because of the thermal stress. (2) High hardness and high toughness of plasma sintered SiC- C composites are presumably due to the residual compressive stress caused by the difference in the thermal expansion coefficient. It is also considered that the toughness was improved by the cracks in graphite grains which inhibited the crack propagation. (3) At the interface between SiC and graphite, there existed the structures that the basal plane of graphite was parallel to the interface, that SiC was transformed near the interface and that SiC had step structures in an amorphous layer formed by reaction on graphite. These structures might be formed to reduce high energy at the interface. A second phase was not observed at grain boundaries in SiC, however, structure relaxation might occur within a thickness of 1 nm.
- 社団法人日本セラミックス協会の論文
- 1989-11-01
著者
-
幾原 雄一
ファインセラミックスセ 試験研
-
幾原 雄一
(財)ファインセラミックスセンター試験研究所
-
陶山 容子
(財)ファインセラミックスセンター
-
木鳥 弌倫
京都工芸繊維大学無機材料工学科
-
陶山 容子
財団法人ファインセラミックスセンター
-
陶山 容子
島根大・物質科学
関連論文
- 21pGE-16 スピネル型LiNi_2O_4における電荷軌道整列相の第一原理計算(21pGE パイロクロア・フラストレーション系,領域8(強相関系:高温超伝導,強相関f電子系など))
- 電子顕微鏡を用いたセラミックスの基礎研究-米国最新情報-
- SiC-Cプラズマ焼結体中のカーボン
- 超硬合金中の炭化タングステン粒界構造
- Bi-Sr-Ca-Cu-O/Ag 複合体の微細構造と機械的性質(セラミックスの合成と評価)
- 2A31 TEM によるセラミックス破壊過程のその場観察
- 18MeV Fe^イオン照射によるBi_2Sr_2CaCu_2O_x超伝導体の特性と微構造の変化
- 石炭灰から合成したゼオライトのアンモニウムイオン吸着特性
- Y_2O_3添加AINにおけるプラズマ焼結温度に関する研究
- 金属アルコキシドからの化学量論組成ムライト超微粉体の合成
- PbTi複合イソプロポキシドからPbTiO_3への生成過程
- セラミックスの評価法-6-(5)粉体--超微粒子の結晶学的性質(セラミックス基礎工学講座)
- ファインセラミックスの化学組成分析法 (ファインセラミックスの最近の動向) -- (セラミックス試験・検査)
- セラミック粉末のキャラクタリゼ-ション (ニュ-セラミック原料粉末の現状)
- 微細構造の体系的・動的その場評価を可能とする新しい評価システム