ジルコニアセラミックスの低温下における強度特性
スポンサーリンク
概要
- 論文の詳細を見る
The influence of temperature on the strength and fracture toughness of ZrO_2-3 mol%; Y_2O_3(YZ-3) ,ZrO_2-6 mol% Y_2O_3(YZ-6), ZrO_2-12 mol%CeO_2(CZ-12) and ZrO_2-14 mol%CeO_2(CZ-14) ceramics was studied from R. T. down to 77 K. The strength was estimated by the three-point-bending method and the fracture toughness was evaluated by the size of initial defects observed on the fracture surface. The bending strength of YZ-3 and YZ-6 increased with decreasing temperature, whereas that of CZ-12 and CZ-14 decreased with decreasing temperature. CZ-12 had a tetragonal to monoclinic transformation temperature from R. T. down to 77 K. Other ceramics had no transformation temperature. The temperature dependence of strength for YZ-3 and YZ-6 agreed with that of fracture toughness.
- 社団法人日本セラミックス協会の論文
- 1990-10-01
著者
関連論文
- 高配向Bi-2223高温超伝導体の磁場中の熱伝導率
- 高配向Bi-2223高温超伝導体の磁場中の熱伝導率(III)
- 5a-Y-3 高配向Bi-2223高温超伝導体の磁場中の熱伝導率(II)
- 12p-PSB-53 高配向Bi-2223高温超伝導体の磁場中の熱伝導率
- 強磁場低温X線回折装置の開発とその応用
- Bi(2223)バルク電流リ-ドの諸特性と冷凍機冷却マグネットへの応用
- 強磁場X線回折装置用Heフリー超伝導マグネットの試作
- 強磁場低温X線回折装置の開発
- Bi系電流リードと4K-GM冷凍機を用いた臨界電流測定装置
- 液体ヘリウムフリー大口径超伝導マグネット : マグネットシステム
- 液体ヘリウムフリー大口径超伝導マグネット : 酸化物電流リード
- 高温超電導材料を用いた磁気シ-ルド円筒の開発
- Ag-7at%CuシースBi-2212多芯線の酸素分圧-Ic特性
- AgシースBi-2212多芯丸線材の試作
- SCM440 およびS45C の破壊じん性に及ぼすオーステナイト化温度の影響
- 30p-PSA-23 Bi系高温超伝導体の輸送現象と散乱機構
- 機械構造用鋼のストレッチ・ゾーン法によるじん性評価
- 高張力鋼母材および溶接部の疲労き裂伝ぱ速度
- 420 X線回析法による爆接クラッド鋼の残留応力の測定
- スタイキャスト補強Bi系(2223)超伝導材料の熱伝導率
- 液体ヘリウムフリー大口径超伝導マグネット
- Bi系酸化物高温超電導電流リ-ドとその応用
- ジルコニアセラミックスの低温下における強度特性
- クラッド鋼の疲労き裂伝ぱ挙動とその破面解析
- 高強度CuNb/(Nb, Ti)_3Snを用いたR&Wコイルの強応力下における曲げ歪みの効果
- 無冷媒23Tハイブリッドマグネットの建設
- 7T/φ220mm-CSM用温度可変型クライオスタットの開発およびBi2223パンケーキコイルの特性
- 7T/?220mm-CSM用冷凍機冷却型温度可変クライオスタットの開発およびBi2223パンケーキコイルの特性
- 高速度鋼射出成形体の強度特性
- 粉末射出成形法により作製したコバ-ル焼結体の特性評価
- 1p-YJ-8 高配向Bi-2223高温超伝導体の磁場中の熱伝導率(IV)(1pYJ 低温(高温超伝導・輸送現象,置換効果),低温)