ホットプレス窒化ケイ素の室温動疲労特性及び強度に及ぼす研削加工の影響
スポンサーリンク
概要
- 論文の詳細を見る
Four-point bending dynamic fatigue tests were carried out at five different crosshead speeds from 5×10^4 to 5 ×10^0 mm/min in air at room temperature. Hot pressed silicon nitride ceramics was used for the tests and ground with 600, 400 and 200 grit resin bonded diamond wheels perpendicular to the direction of bending stress. Both the specimens ground with the 400 and 200 grit wheels showed a decrease in the fatigue parameter and fracture strength, while no decrease was observed in the specimen ground with the 600 grit wheel. It is suggested that grinding induces surface flaws and that the mean fracture strength of specimens ground with the 400 and 200 grit wheels tested at low crosshead speeds is lowered by slow crack growth of the surface flaws which are easily affected by stress corrosion.
- 社団法人日本セラミックス協会の論文
- 1990-11-01
著者
-
久保 勝司
名古屋工業技術試験所
-
兼松 渉
名古屋工業技術研究所
-
山内 幸彦
名古屋工業技術研究所
-
酒井 清介
名古屋工業技術試験所
-
伊藤 正治
名古屋工業技術試験所
-
酒井 清介
名古屋工技試
-
久保 勝司
名古屋工業技術研究所
関連論文
- ぜい性金属の液圧押出しにおける内部き裂の発生 : 第2報,すべり線場理論による解析的検討
- ぜい性金属の液圧押出しにおける内部き裂の発生 : 第1報,実験的検討
- ぜい性金属の液圧押出しにおける内部き裂の発生 : 第2報, すべり線場理論による解析的検討
- ぜい性金属の液圧押出しにおける内部き裂の発生 : 第1報, 実験的検討
- 研削加工された炭化けい素セラミックスの高温酸化
- 窒化ケイ素ウィスカ強化6061アルミニウム基複合材料の超塑性挙動におよぼす押出し比の影響
- 237 熱間押出しにより作製したAl-Mg-Si基複合材料の超塑性挙動(金属基複合材料)
- Si_3N_4ウイスカーあるいは粒子で強化した6061アルミニウム複合材料の高ひずみ速度領域における超塑性挙動
- 3D13 窒化けい素の微構造が摩擦摩耗特性に及ぼす影響
- セラミックスの高温動疲労特性