21/4 Cr-1 Mo鋼のクリープ特性に及ぼす熱処理条件の影響
スポンサーリンク
概要
- 論文の詳細を見る
The influence of heat treatment on the creep properties of 2<1/4> Cr-1 Mo steel were investigated. Comparative creep tests with the duration of 1000 or 2000 hours at 550, 600 and 650℃, were made in the following six different condition s of heat treatment ; that were the normalizing at 900℃, the annealing at 900℃ followed by four different cooling rates of 400℃/hr, 100℃/hr, 25℃/hr and 5℃/hr and the isothermal transformation at 725℃ whose austenitizing temperature was 920℃. Under the stress of 7・5 kg/mm^2 at 600℃, the specimens cooled slowly show larger creep rates. The annealing with the cooling rate of 5℃/hr revealed the largest creep and the normalizing or the annealing with cooling rate of 400℃/hr gave relatively small creep. However, the creep rates of the annealed specimens with slower cooling rates decrease rapidly with the lowering of stress. Under the stress of 3・5kg/mm^2, the largest creep rate were shown by the normalized specimen. The creep strengths for the creep rate of 0・01 per cent per 1000 hours of normalized condition and annealed condition with the cooling rate of 400℃/hr are lower than 2・0kg/mm^2 in spite of their higher creep resistance under the higher stress, and the creep strength of the annealed conditions cooled by 100℃/hr or slower are in the range from 2・8 to 3・0kg/mm^2. Isothermal transformation gave relatively small creep rates in all testing conditions, and the creep strength is the same as in the slowly cooled specimen. The creep test under the higher stress would not be suitable for the criteria of creep strength of the material which is used under the lower stress in service conditions. And the annealing with cooling rate of 100℃/hr or slower or isothermal transformation would be preferable for this steel when they are used as the superheater.
- 社団法人日本材料学会の論文
- 1960-02-15
著者
関連論文
- 119 軸受鋼の地疵成績におよぼす製鋼要因(介在物・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (II))
- 101 球状黒鉛鋳鉄製鋳型の使用(造塊・脱ガス・連鋳・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (I))
- 115 鋼管の拡管加工における Flaking の発生におよぼす諸因子の影響について(加工・性質, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (II))
- 高温用鋼管材料の高温強度
- 238 高温用鋼管材料の高温強度(高温強度, 加工・性質・分析・検査・計測, 日本鉄鋼協会第 84 回(秋季)講演大会)
- 239 長時間使用されたボイラ用鋼管材の高温強度(クリープ・耐熱鋼, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 149 ボイラ用耐熱鋼鋼管の試作とその性質(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 233 オーステナイト系ステンレス鋼中の炭化物生成元素の溶接割れに及ぼす影響について(第2報)
- 232 オーステナイト系ステンレス鋼中の炭化物生成元素の溶接割れにおよぼす影響について(第一報)
- 108 16-13-Mo オーステナイト・ステンレス鋼のクリープ破断特性(加工・耐熱鋼, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 21/4 Cr-1 Mo鋼のクリープ特性に及ぼす熱処理条件の影響
- 88 18-8 Nb ステンレス鋼のクリープ特性(耐熱鋼, 第 59 回(春季)講演大会講演大要)
- 18-8 Ti ステンレス鋼のクリープ特性
- 18-8ステンレス鋼の常温におけるクリープ
- 105 18-8 Ti ステンレス鋼のクリープ特性(耐熱鋼, 第 57 回講演大会講演大要)
- 108 Cr Mo 鋼のクリープ特性に関する研究 (II) : 脱酸条件のクリープ特性におよぼす影響(鉄鋼の性質, 第 55 回講演大会講演大要)
- 73 Cr-Mo 鋼のクリープ特性に関する研究 (I) : 脱酸条件のクリープ特性におよぼす影響(第 53 回講演大会講演大要)