Creep-rupture tests up to about 10, 000h., were carried out with the type 321 stainless steel in the two solution-treated conditions (1050℃ W. Q. and 1200℃ W. Q.) at 600, 650 and 700℃. Stresses and rupture times showed good straight-line relationship up to about 1000h., but beyond that point the line inclined downward. This tendency was more pronominent for 1050℃ W. Q. specimens. Solution-treatment at 1200℃ gave higher rupture strengths for the whole testing conditions. The difference of rupture strength between these two heat treatments was increased with higher temperature and longer time. The shapes of creep curves showed marked difference too. 1200℃ W. Q. specimens were fractured suddenly without any large creep. On the contrary, 1050℃ W. Q. specimens revealed relatively large creep from the early stage and fractured after large elongation. Microstructure of 1050℃ W. Q. specimens fractured at about 2500h. or longer showed the prominent precipitation of σ-phase at grain boundries.
- 社団法人日本鉄鋼協会の論文
- 1960-02-01
著者
関連論文
- 119 軸受鋼の地疵成績におよぼす製鋼要因(介在物・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (II))
- 101 球状黒鉛鋳鉄製鋳型の使用(造塊・脱ガス・連鋳・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (I))
- 115 鋼管の拡管加工における Flaking の発生におよぼす諸因子の影響について(加工・性質, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (II))
- 149 ボイラ用耐熱鋼鋼管の試作とその性質(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 108 16-13-Mo オーステナイト・ステンレス鋼のクリープ破断特性(加工・耐熱鋼, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 21/4 Cr-1 Mo鋼のクリープ特性に及ぼす熱処理条件の影響
- 88 18-8 Nb ステンレス鋼のクリープ特性(耐熱鋼, 第 59 回(春季)講演大会講演大要)
- 18-8 Ti ステンレス鋼のクリープ特性
- 18-8ステンレス鋼の常温におけるクリープ
- 105 18-8 Ti ステンレス鋼のクリープ特性(耐熱鋼, 第 57 回講演大会講演大要)
- 108 Cr Mo 鋼のクリープ特性に関する研究 (II) : 脱酸条件のクリープ特性におよぼす影響(鉄鋼の性質, 第 55 回講演大会講演大要)
- 73 Cr-Mo 鋼のクリープ特性に関する研究 (I) : 脱酸条件のクリープ特性におよぼす影響(第 53 回講演大会講演大要)