18-8ステンレス鋼の常温におけるクリープ
スポンサーリンク
概要
- 論文の詳細を見る
Creep characteristics of 18-8 stainless steel at room temperature were studied. The specimens were fabricated from 20 mm diameter bars, which were cold drawn and solution treated at 1050℃. Constant load creep tests were made under the stresses from 12.5 kg/mm^2 to 50.0 kg/mm^2. Durations of tests were about 2000 hours and the test under 20 kg/mm^2, which is still continued, were conducted over 17000 hours. Under the stresses even lower than the yield strength, relatively large creep was observed and this is advancing even over 10000 hours. In the case of 20 kg/mm^2, instantial elongation was 0.24 per cent, and total elongation reached to 1.3 per cent at 15500 th hour. The creep rate which showed 0.091 per cent per 1000 hours in the interval between 1000 th and 2000 th hour, was reduced to 0.098 per cent per 1000 hours between 10000 th and 17000 th hour. For the test which were conducted under the higher stresses than 20 kg/mm^2, instantial elongation and initial creep rate was greatly increased with stress, but the creep rate at 1000 th hour or after decreased to the similar order of the creep under 20 kg/mm^2. Plottings of logarithm of permanent elongation vs. logarithm of time showed good liner relationship for all these tests and any tendency to deviate from the line to upper side at longer time range, was not detected. It may be concluded that the room temperature creep of this material consist mainly with transient creep, expressed by the formula of dε/dt=αt^<-m>, and no steady creep is contained. From practical point of view, these creep should be taken into account for the design of parts of installations, which should be confined to the small strain. For this purpose, the stresses which produce a definite strain at a certain time were determined from this results. The stress for 0.2 per cent at 1000 th hour is about 75 per cent of the yield strength determined by routine test.
- 社団法人日本材料学会の論文
- 1959-08-15
著者
関連論文
- 119 軸受鋼の地疵成績におよぼす製鋼要因(介在物・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (II))
- 101 球状黒鉛鋳鉄製鋳型の使用(造塊・脱ガス・連鋳・その他, 製鋼, 日本鉄鋼協会第 71 回(春季)講演大会講演論文集 (I))
- 115 鋼管の拡管加工における Flaking の発生におよぼす諸因子の影響について(加工・性質, 日本鉄鋼協会第 67 回(春季)講演大会講演論文集 (II))
- 149 ボイラ用耐熱鋼鋼管の試作とその性質(合金鋼その他, 日本鉄鋼協会第 63 回(春季)講演大会講演大要)
- 108 16-13-Mo オーステナイト・ステンレス鋼のクリープ破断特性(加工・耐熱鋼, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 21/4 Cr-1 Mo鋼のクリープ特性に及ぼす熱処理条件の影響
- 88 18-8 Nb ステンレス鋼のクリープ特性(耐熱鋼, 第 59 回(春季)講演大会講演大要)
- 18-8 Ti ステンレス鋼のクリープ特性
- 18-8ステンレス鋼の常温におけるクリープ
- 105 18-8 Ti ステンレス鋼のクリープ特性(耐熱鋼, 第 57 回講演大会講演大要)
- 108 Cr Mo 鋼のクリープ特性に関する研究 (II) : 脱酸条件のクリープ特性におよぼす影響(鉄鋼の性質, 第 55 回講演大会講演大要)
- 73 Cr-Mo 鋼のクリープ特性に関する研究 (I) : 脱酸条件のクリープ特性におよぼす影響(第 53 回講演大会講演大要)