ポリビニルアルコール皮膜の応力緩和 : 結晶性高分子の構造とレオロジー
スポンサーリンク
概要
- 論文の詳細を見る
In order to gather information on viscoelastic properties of crystalline high polymers, stress relaxation of polyvinyl alcohol (PVA) films were studied. The original films were casted from concentrated solutions of PVA having the viscosity average degree of polymerization (DP) of 2180, 1600 and 600, and had no orientation in the plane of the film. Some of them were heated at 160゜ and 200℃ for 10 minutes to vary the crystallinity from about 20% of the original film to 36.0% and 47.3%, respectively. The degree of crystallinity were evaluated from density measurements. The measurements of the stress relaxation were carried out by employing an Instron Tensile Tester of table model. In order to measure at various temperatures (20゜〜120℃) and relative humidities (0%〜75%), a particular cell was inserted between two jaws of the tester and the sample film was tested in this cell at controlled temperature and humidity. The results obtained are summerized as follows : 1) Original films having DP 2180 and 1600 showed quite the same behavior at 0% and 60% R.H. at 20℃, while the film having DP 600 did somewhat different behavior from the others, though it had almost the same degree of crystallinity. This discrepancy may be attributed to the difference in its fine structure from the others. 2) Original films of DP 2180 and 600 were tested at 20℃ over a wide range of relative humidity, and a notable dispersion was found near 50% R.H. for both of the films. Relaxation modulus against logarithm of time at various R.H. can be superposed by horizontal shift of the curves along the log time axis to give a composite curve at any reference humidity. The relaxation spectrum calculated from the composite curve referred to 0% R.H. ranged from 0 to 10^<15> sec, and showed good agreement with that obtained by Kawai et al. from the dynamic data over a range of 10^3 to 10^8 sec. Although our spectrum ranged to very long time, any flow region was not observed. 3) Heat-treated film having DP 2180 and degree of crystanity 47.3% was tested in a temperature range from 20℃ to 120℃. The time-temperature superposition principle was not valid for the result. Qualitatively speaking, it seemed that for PVA film there appeared many dispersions in glassy state differing from the cases of amorphous polymers. 4) The effect of crystallinity on sterss relaxation were studied with two samples having the degree of crystallinity of 36.0% and 47.3%, respectively. Although the phehomena observed were too complicated to discuss quantitatively, it was clear that the effect appeared only in the dispersion regions.
- 社団法人日本材料学会の論文
- 1959-04-15
著者
関連論文
- ポリスチレン濃厚溶液の粘度と分子量の関係に及ぼす溶媒の影響
- 数種の高分子物質の動的復屈折の周波数依存性
- 高分子物質の動的複屈折に関する研究(第2報) : 応力-ひずみ-複屈折図の解析
- 6本の枝をもつ星形ポリスチレンとその濃厚溶液の粘弾性的性質
- 星形に枝分れしたポリスチレン濃厚溶液の粘弾性
- ランダムに枝分れしたポリスチレン濃厚溶液の粘弾性
- 新しい混合則と高分子混合物の粘弾性に及ぼす分子量と混合割合の影響
- 分散系にみられる非線形粘弾性の解析法
- 高分子ー粒子混合系の粘弾性
- 数種の懸濁液の流動特性
- 応力-ひずみ-赤外二色性の同時測定による高密度ポリエチレンおよびポリプロピレンの変形機構の研究
- レオロジー特集号の刊行にあたって
- 高分子溶融物の粘弾性測定を主眼とするレオメーターの試作 : レオロジー一般
- ポリスチレン溶液-球形粒子分散系の長いタイムスケールにおけるレオロジー的性質
- ポリエチレン溶液-ラテックス分散系の非線形粘弾性
- ポリスチレン溶液-ラテックス分散系のレオロジー的性質
- Flexible Polyurethane Foams: Chemistry and Technology, 軟質ポリウレタン発泡体 : 化学と技術, George Woods(著), (1982年, Applied Science Pub. Co. 発刊, 155×230mm, xii+334ページ, £28.00)
- 高分子材料 : 新しい高分子材料(高強度繊維,伝導性高分子,複合材料など)("材料はどこまで進むか"-極限状態と高性能,新機能への挑戦-)
- The Physics of Glassy Polymers (Materials Science Series), ガラス状高分子の物理, (R.N. Haward編著, Applied Science Publishers 1973年刊, サイズ148×230mm, 620ページ, 13,200円)
- 低密度ポリエチレンの非線形粘弾性領域における流動光学的研究
- エチレン-イソプレンA-B型ブロック共重合体の粘弾性および流動光学的性質
- 融解状態で混合されたポリエチレンーポリプロピレン系の赤外二色性と粘弾性
- 低密度ポリエチレンの複屈折の時間依存性
- 応力-ひずみ-赤外吸収同時測定による低密度ポリエチレン変形機構に関する研究
- 高分子濃厚溶液の非ニュートン流 : I. ポリビニルアルコール水溶液 : 高分子レオロジー
- 高分子溶融物の粘弾性と混合比の関係
- ポリエチレン溶融物における定常流粘度と動的粘度との比較 : 高分子液体の流動性
- 高分子濃厚溶液の非ニュートン流 : II. ポリスチレンのトルエン溶液 : 高分子レオロジー
- 高密度ポリエチレンの複屈折の時間依存性に対する時間-温度の重ね合わせ
- ポリエチレンの溶融粘弾性
- 高分子機械材料ナイロン樹脂ガイドブック, 高分子学会高分子機械材料委員会編, A5版, 338ページ, 1,500円, 昭和39年7月5日, 共立出版株式会社発行
- ポリビニルアルコール皮膜の応力緩和 : 結晶性高分子の構造とレオロジー
- 高密度ポリエチレンの力学的および流動光学的性質の時間-温度重ね合わせにおける垂直移動の機構について (レオロジー(特集))
- 分散系にみられる非線形粘弾性 (レオロジー(特集))
- Cyperus Papyrus