各種高強度鋼材の変動応力下における遅れ破壊
スポンサーリンク
概要
- 論文の詳細を見る
The effect of superposition of small repeating stress on σ_<sec> the endurance stress under which no crack initiation occurs within 100h, and on the incubation time (time of crack initiation) has been investigated using notched specimens of four kinds of steels (JIS : SKD61, SNCM8, SUS420J2, and 18Ni maraging steel) quenched and tempered at various temperatures. The results obtained are as follows : (1) For all the steels examined, the endurance stress σ_<sec> was not varied by the superposition of repeating stress when the stress amplitude, σ_a, was 2.5kg/mm^2, when σ_a was larger than 5kg/mm^2, however, σ_<sec> decreased with increase of σ_a. (2) The amount of decrease of σ_<sec> by the superposition of repeating stress seemed to be dependent not only on the yield strength of the materials but also on the stability of protective film on the notch surface against repeating stress and the intensity of metal-environment corrosion reaction after the destruction of the protective film by repeating stress. 18Ni maraging steel and SUS420J2 stainless steel with higher value of σ_<sec> under static stress revealed the smaller decrease of σ_<sec> under repeating stress than SKD61 and SNCM8 steels.
- 社団法人日本鉄鋼協会の論文
- 1979-04-01
著者
関連論文
- 609 サーメットコーティングした軟鋼の腐食と疲労に関する研究(表面処理I,疲労破壊の防止と評価,オーガナイスドセッション1)
- レーザレンジファインダによる溶射皮膜のはく離状態と3次元位置の同時検出(機械力学,計測,自動制御)
- 3次元計測器を用いた手舟状骨形態の検討
- SUS304鋼表面でのミクロな大気汚染物の付着および紫外線・オゾン処理によるそれらの除去
- すき間を有するSUS304ステンレス鋼の腐食挙動に及ぼす超音波印加の影響
- Si_3N_4セラミックスの機械的特性および親油性に及ぼすSiO_2添加の影響
- 純チタンおよびチタン合金の水溶液下での腐食と水濡れ性の基礎的解析
- 純チタンおよびチタン合金のNaF水溶液浸漬による水濡れ性の変化
- 硫酸液滴の付着量が純鉄表面の腐食挙動に及ぼす影響
- セラミックス溶射材の静荷重下および繰返し荷重下での表面ひずみとはく離生成