A study has been made of the diffusion behavior of electrodeposited nickel on various plain carbon steels. Influences of carbon contents in the various steels used as substrate, heat treatment temperature and holding time on the structure, composition, hardness are of produced diffusion layer are described. The results are summerized as follows ; 1) The diffusion layer is formed even after heat treatment at a comparatively low temperature such as 600℃. 2) The diffusion occurs by volume diffusion process in the temperature range between 600℃ and 800℃, while it occurs by grain boundary diffusion process in the temperature range between 900℃ and 1000℃. 3) Some carbides are observed in the diffusion layer, but the kind and type of carbides were not determined by X-ray diffraction in the all steels tested has a comparatively good resistance against nitric acid, and its hardness is as low as 170 in knoop handness.
- 社団法人日本鉄鋼協会の論文
- 1976-10-01
著者
関連論文
- 12・2 加工技術の研究状況(12.切削・工作機械,機械工学年鑑)
- 光沢Ni-Crめっき鋼板の屋外暴露試験による腐食特性についての統計的評価
- 光沢Ni-Crめっき鋼板のCASS試験による腐食特性についての解析
- アルミニウムのアルカリ性化学研磨液における浴組成と光沢度, 表面構造との関係について
- 新年にあたって
- りん酸による銅の電解研磨における銅イオンの影響
- 機能めっきによる改質 (表面改質)
- 電解焼入れにおける電位-電流曲線の解析
- 電解浸炭性に及ぼす浴組成の影響
- アルミニウム陽極酸化皮膜の限界膜厚
- シュウ酸浴によるアルミニウムの高速陽極酸化
- Al合金の陽極酸化に及ぼすSiの影響
- めっき・拡散処理
- 電析による複合材料(非金属材料)
- 強制流動下におけるアルミニウムの陽極酸化時の焼け現象
- アルミニウムの陽極酸化時の焼けに及ぼす電解条件の影響
- 電析ニッケル : 炭素鋼拡散対における拡散層の状態
- 電析クロム-炭素鋼拡散対における拡散層の状態
- 電析ニッケル-鉄拡散対における拡散層の状態について
- 電析クロム-ニッケル拡散対における拡散層の状態について
- 280 各種炭素鋼-クロム, 各種炭素鋼-ニッケルの固相拡散について(表面処理・マルエージ鋼, 性質, 日本鉄鋼協会 第 87 回(春季)講演大会)
- Distribution of the Number of Pits on Bright Ni-Cr Electrodeposited Steel Panels Subjected to the CASS Test.
- Chromium contents in anodic oxide films formed on Al in chromic acid solution.