電析クロム-炭素鋼拡散対における拡散層の状態
スポンサーリンク
概要
- 論文の詳細を見る
Investigations have been carried out on steel/chromium diffusion couples, which were prepared by electrodepositing chromium on various plain carbon steels. Influences of carbon contents in the steels used as materials, of heat treatment temperature, and of holding time on the structure, composition, hardness etc., of produced diffusion layer were studied. The results are summarized as follows : 1) The diffusion layer is formed even after heat treatment at a comparatively low temperature such as 600℃. On all the steels, the produced diffusion layers are of about 85% in Cr concentration. 2) When heat-treated at a higher temperature than 800℃, the steel has a diffusion layer of the composition different from that in (1), the layer being of about 75% in Cr concentration. In this system, as the material contains carbon, the produced polyphase diffusion layer is different from that observed in the Fe-Cr system and changes according to the temperature range. 3) Formation of the diffusion layer hardly depends on carbon content of the material and the thickness of the layer is almost constant for all the carbon contents. 4) In the diffusion layer of a high Cr concentration, carbon is locally saturated and the layers of constant-carbon cencentration are formed which contain more carbon than in the steel. It appears that, chromium carbide and double carbide of iron and chromium may be formed but the existence of those carbides could not be proved by X-ray diffraction, perhaps because of their too small amounts. 5) The produced diffusion layer has a comparatively good resistance against hydrochloric acid, picric acid etc., and its hardness, as one of mechanical properties, is as high as 1000 or more in H_K, which may be typical of carbide.
- 社団法人日本鉄鋼協会の論文
- 1976-03-01
著者
関連論文
- 12・2 加工技術の研究状況(12.切削・工作機械,機械工学年鑑)
- 光沢Ni-Crめっき鋼板の屋外暴露試験による腐食特性についての統計的評価
- 光沢Ni-Crめっき鋼板のCASS試験による腐食特性についての解析
- アルミニウムのアルカリ性化学研磨液における浴組成と光沢度, 表面構造との関係について
- 新年にあたって
- りん酸による銅の電解研磨における銅イオンの影響
- 機能めっきによる改質 (表面改質)
- 電解焼入れにおける電位-電流曲線の解析
- 電解浸炭性に及ぼす浴組成の影響
- アルミニウム陽極酸化皮膜の限界膜厚
- シュウ酸浴によるアルミニウムの高速陽極酸化
- Al合金の陽極酸化に及ぼすSiの影響
- めっき・拡散処理
- 電析による複合材料(非金属材料)
- 強制流動下におけるアルミニウムの陽極酸化時の焼け現象
- アルミニウムの陽極酸化時の焼けに及ぼす電解条件の影響
- 電析ニッケル : 炭素鋼拡散対における拡散層の状態
- 電析クロム-炭素鋼拡散対における拡散層の状態
- 電析ニッケル-鉄拡散対における拡散層の状態について
- 電析クロム-ニッケル拡散対における拡散層の状態について
- 280 各種炭素鋼-クロム, 各種炭素鋼-ニッケルの固相拡散について(表面処理・マルエージ鋼, 性質, 日本鉄鋼協会 第 87 回(春季)講演大会)
- Distribution of the Number of Pits on Bright Ni-Cr Electrodeposited Steel Panels Subjected to the CASS Test.
- Chromium contents in anodic oxide films formed on Al in chromic acid solution.