溶鋼中炭素によるCr_2O_3含有スラグのクロム還元速度に及ぼすスラグ性状の影響

概要

論文の詳細を見る
The experiments were performed using a small-scale furnace in order to improve the reduction rate of chromium oxide in Cr_2O_3 containing slag by carbon in steel. As a result of the investigation of the experiments by SOLGASMIX, the following points were clarified:1) The reduction rate of chromium oxide in slag was improved by lowering the basicity of the slag or by adding AL_2O_3 or CaF_2. This improvement was caused by the increase of liquid phase fraction of the slag.2) The liquid fraction of the slag was related to the increase of the mass transfer coefficient and/or the effective reaction area of reaction.3) The dissolution of MgO was accelerated greatly by lowering the basicity or by adding CaF_2. This phenomenon was caused by the increase of MgO solubility in the slag.4) The optimum composition of slag is (Al_2O_3)=15% and CaO/SiO_2=2.5 from the viewpoint of the compatibility of the improvement of reduction rate of chromium oxide and the prevention of the dissolution of the refractories.
社団法人日本鉄鋼協会の論文
2002-12-01