金属鉄生成以前におけるウスタイトの CO ガス還元の混合律速モデルによる速度解析

概要

論文の詳細を見る
Dense wustite plates have been reduced at 1273K with CO-CO_2 gas mixture which has a chemical potential to form metallic iron. In early stage of the reduction, no formation of metallic iron was observed and only the composition of the wustite changed. The composition change was followed by the changes of the lattice parameter and the mass of the sample. A mixed chemical reaction/solid state diffusion limited model was applied to the reduction rate. The reduction rate r was expressed by the following equation, r=k′・(1-α/K_S)・P_<CO>(kg-oxygen/m^2・s) where K_S and α are the P_<CO_2>/P_<CO> ratio in the gas mixture in equilibrium with the surface wustite and that in the reducing gas mixture, respectively. The apparent chemical reaction rate constant k′ changed with K_S and was expressed as follows, k′=1.18×10^<-10>・K_S^<0.34>(kg-oxygen/m^2・s・Pa). On the other hand, the inter-diffusion coefficient D^^∿ was independent of the iron ion vacancy concentration y and was estimated as D^^∿=5.4×10^<-10>(m^2/s) at 1273K. The iron ion concentration profile, estimated from the lattice parameter, and the mass change of the reduced wustite were explained reasonably by the model.
社団法人日本鉄鋼協会の論文
1995-11-01