Cr 含有鋼への Cr 拡散浸透処理層の組成と耐食性に及ぼす鋼中の Cr と固溶 C の影響

概要

論文の詳細を見る
The effects of C and Cr on the chromium diffusion layer formation by pack comentation process on Cr alloy steels (Cr : 2.25 mass%-12 mass%) were examined. The following results were obtained. (1) The structure of chromium diffusion coating on alloys which contained free C consisted of two layers independent of Cr content on alloys. The outer layer was chromium carbide film consisting of Cr_<23>C_6 and Cr_7C_3. The inner layer was Cr diffusion layer whose Cr content ranged from 25 mass% to 13 mass%. (2) The thickness of Cr diffusion coating significantly depended on the free C and Cr content in alloy. The thickness of chromium carbide film, increased with increasing C content in alloy. On the other hand, the thickness of Cr diffusion layer increased with decreasing C content and increasing Cr content in alloy. (3) The outer chromium carbide film and inner Cr diffusion layer exhibited good oxidation resistance in super heated steam environment due to the formation of Cr_2O_3 scale on both layers.
社団法人日本鉄鋼協会の論文
1991-08-01