Nb 添加熱延鋼板の機械的性質におよぼす Sol. Nb 量の影響

概要

論文の詳細を見る
The precipitation behavior of Nb in deformed austenite and the effect of precipitation on rolling load and mechanical properties were studied in two Nb treated steels and a Nb free steel. The steel slabs were solution treated at 1250℃, hot rolled in a five pass schedule and cooled at 40℃/s. Precipitation treatment of Nb was performed between third and fourth passes at 950℃ for 0∿20min. Nb (CN) was quantitatively analysed as Insol. Nb by using electrolysis method. Sol. Nb (Total Nb-Insol. Nb), rolling load and tensile strength (TS) decrease with holding time at 950℃. The decreasing rate of these values measured for 0.03%Nb steel are larger than that for 0.02%Nb steel. This result shows that the amount of Nb disolved in austenite accelerates the rate of precipitation. TS increase with increasing Sol. Nb and in case of 0.03%Nb steel the increment of TS depending on an increase in precipitation hardening in ferrite is estimated at 12kgf/mm^2. These results show that Sol. Nb is able to be used for the prediction of the mechanical properties of Nb treated hot rolled steel sheet.
社団法人日本鉄鋼協会の論文
1991-05-01