高 Cr-Ni オーステナイト鋼の高温疲労強度 : 高 Cr-Ni オーステナイト鋼の研究 II
スポンサーリンク
概要
- 論文の詳細を見る
Effect of alloying elements, melting process, heat treatments and grain size on high-temperature fatigue strength were investigated with AISI type 309, 310 and 330 steels to obtain some practical design data. The results obtained were discussed on the basis of precipitation hardening of austenite. In this experiment tests were carried out at 650℃, 800℃ and room temperature, using a rotary bending fatigue testing machine. The results obtained are as follows : (1) There is a definite fatigue limit at 650℃ which is higher than the proof strength at this temperature, and this fact is explained by precipitation hardening of austenite. But no definite fatigue limit is observed at 800℃. (2) The endurance ratio at 650℃ is considerably higher than that at room temperature. This indicates that the strengthening of austenite due to precipitation takes place during the fatigue test at this testing temperature. (3) At 650℃ the fatigue limit is lower than the creep rupture strength obtained from a short-time rupture test (up to 10 h). But the creep rupture strength for long-time test (more than 10 h) are lower than the fatigue limit. The creep rupture strength, therefore, is more important than the fatigue strength in determining the working stress of a high-temperature machine elements. (4) Carbon and nitrogen are very effective elements in improving the fatigue strength of these steels, while silicon and nickel have a minor effect, but no effect is observed with chromium. (5) Specimens melted in vacuum shows little influence on the fatigue strength as compared with that melted in air of the corresponding chemical analysis. (6) As the temperature of the solution treatment of specimen is raised up to 1200℃, the fatigue strength of type 309 and 310 steels is increased even though there is a considerable grain growth. (7) The fatigue strength at 650℃ of austenitic stainless steels is controlled not only by the resistance of plastic deformation of austenite but also by the precipitation hardening which takes place in austenitic matrix during repeated loadings.
- 1962-01-01
著者
関連論文
- 18-8系ステンレス鋼の切欠クリープ破断強度について
- 17-7PHステンレス鋼の応用時効処理による強度変化について
- 不銹鋼の応力腐食割れに及ぼす加工の影響
- オーステナイト系不銹鋼の高温における二,三の強度特性と組織の変化
- 鋼の応力におよぼす炭素量の影響について
- 低温焼入による鋼の材質の変化について : 第8報 鋼の時効硬化能と切欠疲労強度
- 低温焼入による鋼の材質の変化について : (第5報)鋼の時効硬化能と疲れ強さ
- 低温焼入による鋼の材質の変化について : (第5報)鋼の時効硬化能と疲れ強さ
- 低温焼入れによる鋼の材質の変化について : (第4報)切欠き疲れ強さの改善
- 低温焼入による鋼の材質の変化について(第3報) : 疲労および衝撃強度の改善
- 低温焼入による鋼の材質の変化について : (第4報)切欠疲れ強さの改善
- 常温以上の温度で加工した軟鋼の低温焼鈍の影響 (続報)
- 低温焼入による鋼の材質の変化について (第2報) : 中炭素鋼の疲れ強度および衝撃強度
- 高 Cr-Ni オーステナイト鋼の高温疲労強度 : 高 Cr-Ni オーステナイト鋼の研究 II
- 軟鋼の応力時効に就いて
- 軟鋼の磁性に及ぼす応力の影響
- 軟鋼の磁性に及ぼす加工並びに焼鈍の影響
- 軟鋼の磁性に及ぼす應力の影響
- 高 Cr-Ni オーステナイト鋼の高温変形能 : 高 Cr-Ni オーステナイト鋼の研究 I
- 高 Cr フェライト鋼の高温変形能
- 91 LCN-155 板の機械的性質について(耐熱鋼, 第 59 回(春季)講演大会講演大要)
- 94 真空アーク溶解による偏平鋼塊について(製鋼造塊, 日本鉄鋼協会第 66 回(秋季)講演大会講演大要)
- 104 高 Cr-Ni オーステナイト鋼の高温強度におよぼす時効処理の影響 : 高 Cr-Ni オーステナイト鋼の研究 IV(加工・耐熱鋼, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 高Cr-Niオーステナイト鋼の高温強度
- 171 高 Cr-Ni オーステナイト鋼の高温疲労強度 : 高 Cr-Ni オーステナイト鋼の研究 III(性質・ステンレスおよび耐熱鋼, 日本鉄鋼協会第 61 回講演大会講演大要)