軸受鋼のリング壓壞値について : 軸受鋼の研究 II
スポンサーリンク
概要
- 論文の詳細を見る
(1) To substitute the bend fracture test of flat test pieces (flat 10×20×length 55mm, distance between the two supporting points 40mm) at the place of ring crushing test (standard size of rings : outer dia. 80×inner dia 60×height 20mm) of the ball bearing steels, the author studied experimentally the relation between the crushing strength P and the bend fracture strength Q, measuring the both in parallel, changing the quenching and tempering temperatures, with the ring and flat test pieces, both shaped out and forged. (2) Then the author calculated the relation equation between P and Q, considering the test pieces as the perfect elastic body. From the idea that the test pieces broke when the max. tensile skin stress on the section at the loading point increased beyond the strength of this material, the author obtained P/Q≒0.806α From the idea that the test pieces broke when the deformation energy on the section at the loading point increased beyond a limit value, the author obtained P/Q≒0.890α′where α and α′were the coefficients which were determined according with their manufacturing conditions, for example, fibre direction etc. (3) Next the author determined the values α and α′so that these theoretical equations accommodated well with the values practically measured. Considering the statistically measured results of the forged test pieces from the production billets of about 110 charges, rather than the test results of the several charges above mentioned in (1), the author obtained α=0.85 and α′=0.75. Then P≒0.6763 Q : so, when P=4, 000 kg, Q≒6, 000 kg. By these data, the author proposed to substitute the bend fracture test of flat test pieces in place of ring crushing test and to define that the bend fracture strength must be more than 6, 000 kg. (4) The author checked the coefficient α by means of the resistance wire type strain gauge. (5) The author checked the relations between the size of rings and their crushing strengths theoretically obtained, comparing with the values practically measured. (7) At last, the author studied the influences of rolling or forging conditions of the billets etc. on their ring crushing strengths.
- 社団法人日本鉄鋼協会の論文
- 1953-10-25
著者
関連論文
- リムを超耐熱鋼 LCN-155 で作れる大型複合車盤の製造研究
- 136 リムを超耐熱鋼 LCN-155 で作れる大型複合車盤の製造研究(第 52 回講演大会講演大要)
- 耐熱鋼-5-
- 耐熱鋼-4-
- 耐熱鋼-3-
- 耐熱鋼-2-
- 耐熱鋼-8-
- 耐熱鋼-7-
- 耐熱鋼-6-
- 軸受鋼材に現わるゝ粗大炭化物について : 軸受鋼の研究第 1 報
- 85 エレクトロスラグ法による高合金鋼の溶解(製鋼反応・エレクトロスラグ溶解, 日本鉄鋼協会第 69 回(春季)講演大会講演論文集 (I))
- 91 軸受鋼の合成鋼滓処理(電気炉・平炉・溶銑予備処理・耐火物, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (I))
- 142 熔解原料が軸受鋼におよぼす影響について(性質, 日本鉄鋼協会第 61 回講演大会講演大要)
- 軸受鋼 SUJ 3 ころ材に発生する白雲状に見える微小砂疵について
- Mo-V 低合金耐熱鋼の系統的研究
- 125 Mo-V 低合金耐熱鋼の基礎的研究(低合金鋼ほか, 第 58 回講演大会講演大要)
- 軸受鋼中の A 系非金属介在物の電子顕微鏡的考察
- 84 軸受鋼 SUJ 3 ころ材に発生する白雲状砂疵について(軸受鋼・その他, 第 57 回講演大会講演大要)
- 塩基性エルー電弧炉々床ライニングの基礎的調査報告
- 89 軸受鋼中の A 系非金属介在物の電子顕微鏡的考察(快削鋼・軸受鋼・構造用鋼の諸性質, 日本鉄鋼協会第 56 回(秋季)講演大会講演大要)
- 19 塩基性エルー電弧炉々床ライニングの基礎的調査報告(製鋼, 第 55 回講演大会講演大要)
- 57 輔受鋼の炭化物偏析に関する研究(追補) : 軸受鋼の研究第 4 報(第 49 回講演大会講演大要)
- LCN-155 における N, Cb の影響および S-816 における Cb の影響(続) : 耐熱鋼の研究 第 10 報 その 2
- LCN-155 における N, Cb の影響および S-816 における Cb の影響 : 耐熱鋼の研究第 10 報その 1
- 軸受鋼のリング壓壞値等に及ぼす不純物の影響 : 軸受鋼の研究 III
- 71 耐熱鋼の研究 (X) : LCN-155 における N, Cb の影響 S-816 における Cb の影響(日本鐵鋼協會第 47 囘講演大會講演大要)
- Timken16-25-6耐熱鋼について
- 軸受鋼のリング壓壞値について : 軸受鋼の研究 II
- 各種工具鋼の燒戻による硬度と靱性の變化
- 熱間工具鋼の研究
- 特殊耐熱鋼の高温度特性研究
- 13 軸受鋼に關する研究 (II-III)(日本鐵鋼協會第 45 回講演大會講演大要)
- Timken 16-25-6 耐熱鋼に及ぼす N の影響並にその電子顯微鏡的考察 : 耐熱鋼の研究 IX
- 13 Timken 16-25-6 耐熱鋼に及ぼす N の影響並にその電子顯微鏡的考察 : 耐熱鋼の研究 IX(日本鐵鋼協會第 44 回講演大會講演大要)
- ガスタービン翼用耐熱鋼に關する研究 II : 耐熱鋼の研究 VIII
- ガスタービン翼用耐熱鋼に關する研究 (I) : 耐熱鋼の研究 VIII
- 含窒素高 Mn-Cr 鋼の研究
- Cr-W 鋼に及ぼす C の影響 : 熱間工具鋼の研究の續報
- 耐熱構造用鋼の研究 : 耐熱鋼の研究 (VI)
- 高 Mn-Cr 耐熱鋼の機械的性質に關する研究 II : 耐熱鋼の研究 V
- 高 Mn-Cr 耐熱鋼の機械的性質に關する研究 (I) : 耐熱鋼の研究 IV