異方性 MK 磁石の研究 (I) : 組成及び添加元素の影響
スポンサーリンク
概要
- 論文の詳細を見る
The MK permanent magnet Fe-Ni-Al ternary aloy was invented by Tokushichi Mishima (one of authors) in 1930. Since then the magnetic properties of this alloy underwent no improvement to a remarkable degree for sometime. During the 2nd World War, it was discovered that MK magnet containing the certain restricted range of composition could attain to excellent magnetic properties by the heat-treatment in magnetic field. In our country, the investigation of the magnetic treatment of MK magnet was kept on for a long time in Mishima's laboratory in University of Tokyo. In this report, the results of such investigation on the effects of chemical composition and additional elements on the magnetic properties of this anisotropic MK magnet alloy will be described. The experimental results on the heat-treatment and industrial aspects may be reported later. Briefly this report may be summarized as follows : According to the increase of Ni content up to 17%, the coercive force is improved, but the residual induction becomes inferior. Increase of Co content up to 28% is preferable for the residual induction, but its content is relative to Ni content and it is desirable to restrict the total content of Ni and Co to 38 or 39%. The magnetic properties is sensitive to Al content. The optimum composition is 7.8∿8.4% and unfavourable effects become marked when Al contents reach to less than 7%. The optimum chemical composition of Al needs to be changed according to the additional Si and Ti contents. C content has to be kept under 0.05%, because it is apt to cause a remarkable deterioration of the magnetic properties. Addition of Ti is effective in overcoming its undesirable effects. As Si, Mn and P ill-effect on the magnetic properties, it is advisable that Si, Mn and P contents should be kept respectively lower than 0.2%, 0.3% and 0.02%. Addition of Cb and Zr is favourable to the magnetic properties, especially Cb is effective to improve the coercive force. The effects of other additional elements : B, Cr, W, Mo, V, Be and Sn, is unpreferable to the magnetic properties.
- 1956-11-01
著者
関連論文
- 異方性 MK 磁石の研究 (I) : 組成及び添加元素の影響
- 永久磁石の研究とその問題点
- 最近の永久磁石 (II)
- 最近の永久磁石 (I)
- MT 磁石の工業化に関する実験 (III) : 磁気的特性および工業的応用について
- MT 磁石の工業化に関する実験 (II) : 熱処理の影響と組織について
- MT 磁石の工業化に関する実験 (I) : 合金成分および添加元素の影響
- 異方性 MK 磁石の研究 (III) : 磁気的特性および工業的応用
- 異方性 MK 磁石の研究 (II) : 熱処理と組織について
- 耐久磁石合金の研究 (IV) : 各種磁石鋼の時効硬化機構に就いて
- 耐久磁石合金の研究 (II) : 冷間加工せる高 Mn 鋼の磁性に就いて
- 耐久磁石合金の研究 (1) : アルミニウム炭素鐵系合金の磁性に就いて
- 将来の鉄鋼研究体制について
- 創立 60 周年を迎えて
- 追悼の辞
- 欧米の鉄鋼視察報告
- 新年を迎えて
- 西欧における鉄鋼業視察報告
- 再び会長に選らばれて
- 年頭の辞
- 金属と文化
- 本邦に於ける鉄鋼研究最近の進歩
- 歐洲視察報告 (II)
- 歐洲視察報告 (I)
- 研究と産業の連絡の強化
- 第 9 班(冶金研究關係)(第 1 回世界冶金會議)
- 合金磁気記録用材料