MT 磁石の工業化に関する実験 (III) : 磁気的特性および工業的応用について
スポンサーリンク
概要
- 論文の詳細を見る
Fe-Al-C permanent magnet alloy, the products of which have been produced since 1947 under the commercial name of MT magnets, is the unique magnet alloy which possesses comparatively high coercive force of 200 Oersteds containing none of rare metals. In this report, there will be dealt with the results of experiments relative to industrial aspects which are believed necessary to be known by customers, with special emphasis on those basic magnetic properties and experimental data on demagnetization in additions to industrial applications. The essential magnetic properties are listed in Table 1. The residual induction of MT magnet is nearly equal to one of MK or NKS magnet and the coercive force is nearly equal to one of high Co steel. The stability of magnetic induction over extended period of time is very important in case of electrical instruments or meters. The magnetic aging may be due either to structural change and thermal fluctuation or to external demagnetizing influences such as stray field, mechanical shock, heating or change of reluctance. Effects of various demagnetizing factors on the magnetic stability were investigated accordingly. In all cases this magnetic change can be related to time and external actions in a logarithmic form. Magnetic aging will be stabilized by means of the previous demagnetizing of alternative field and heating. Thermal coefficient of this alloy for the watt-hour meter is -4.0×10^<-4>/℃ and is considerably larger than one of chrome steel. The application of this magnet to industrial fleld is now being expanded. Among its applications, some are now developed to commercial production with great success. The representative examples of industrial uses are mentioned. By the performance tests of MT and Cr steel for watt-hour meters, it was proved that MT is more stable against demagnetization and maintains higher magnetic flux even with its less weight.
- 社団法人日本鉄鋼協会の論文
- 1957-07-01
著者
関連論文
- 異方性 MK 磁石の研究 (I) : 組成及び添加元素の影響
- 永久磁石の研究とその問題点
- 最近の永久磁石 (II)
- 最近の永久磁石 (I)
- MT 磁石の工業化に関する実験 (III) : 磁気的特性および工業的応用について
- MT 磁石の工業化に関する実験 (II) : 熱処理の影響と組織について
- MT 磁石の工業化に関する実験 (I) : 合金成分および添加元素の影響
- 異方性 MK 磁石の研究 (III) : 磁気的特性および工業的応用
- 異方性 MK 磁石の研究 (II) : 熱処理と組織について
- 耐久磁石合金の研究 (IV) : 各種磁石鋼の時効硬化機構に就いて
- 耐久磁石合金の研究 (II) : 冷間加工せる高 Mn 鋼の磁性に就いて
- 耐久磁石合金の研究 (1) : アルミニウム炭素鐵系合金の磁性に就いて
- 将来の鉄鋼研究体制について
- 創立 60 周年を迎えて
- 追悼の辞
- 欧米の鉄鋼視察報告
- 新年を迎えて
- 西欧における鉄鋼業視察報告
- 再び会長に選らばれて
- 年頭の辞
- 金属と文化
- 本邦に於ける鉄鋼研究最近の進歩
- 歐洲視察報告 (II)
- 歐洲視察報告 (I)
- 研究と産業の連絡の強化
- 第 9 班(冶金研究關係)(第 1 回世界冶金會議)
- 合金磁気記録用材料