耐久磁石合金の研究 (IV) : 各種磁石鋼の時効硬化機構に就いて
スポンサーリンク
概要
- 論文の詳細を見る
The ageing mechanism of various permanent magnets : namely, M.K. Steel, Cunifealloy, Kosteralloy, Fe-Al-C alloy and Fe-Mn alloy were invetigated. From the changes of magnetic properties, hardness, Xray-and Micro-structures by tempering of quenched samples at proper temperatures, we obtained the following results. (1) In Fe-Mn alloy, the hardened state is caused by the dispersion of austenite in martensite, formed by cold-working. (2) In Koster alloy, the hardening proceeds with the precipitation of the compound and in the maximum hardened state, the precipitation is already completed. (3) In Cunife alloy, the maximum hardened state is obtained after the precipitated 2 phases coagulate. (4) In Fe-Al=C alloy, the primary hardening is caused by the austenite-martensite transformation and the secondary hardening by the precipitation of the double carbide. (5) In M.K. Steel, the precipitation of the 2 phases (α.α′) do not occur, and it hardens as the preliminary process of the precipitation. Then the tempering curve of M.K. steel was drawn, and the activation energy of ageing was calculated.
- 社団法人日本鉄鋼協会の論文
- 1950-05-25
著者
関連論文
- 異方性 MK 磁石の研究 (I) : 組成及び添加元素の影響
- 永久磁石の研究とその問題点
- 最近の永久磁石 (II)
- 最近の永久磁石 (I)
- MT 磁石の工業化に関する実験 (III) : 磁気的特性および工業的応用について
- MT 磁石の工業化に関する実験 (II) : 熱処理の影響と組織について
- MT 磁石の工業化に関する実験 (I) : 合金成分および添加元素の影響
- 異方性 MK 磁石の研究 (III) : 磁気的特性および工業的応用
- 異方性 MK 磁石の研究 (II) : 熱処理と組織について
- 耐久磁石合金の研究 (IV) : 各種磁石鋼の時効硬化機構に就いて
- 耐久磁石合金の研究 (II) : 冷間加工せる高 Mn 鋼の磁性に就いて
- 耐久磁石合金の研究 (1) : アルミニウム炭素鐵系合金の磁性に就いて
- 鐵及び鐵合金の高温酸化に關する研究 (VII) : Fe-Al, Fe-Cr-Al, Fe-Si 各合金の酸化物被覆について
- 鐵及び鐵合金の高温酸化に關する研究 (VI) : Fe-Cr 合金の酸化物被覆の構造
- 鐵及び鐵合金の高温酸化に關する研究 (V) : 耐酸化限界温度について
- 鐵鋼中に於けるジルコニウム
- Cr 鋼滲炭層の特性とその熱處理による改善
- 特殊鋼のオーステナイト粒子生長の特性 (II)