耐熱合金 Timken 16-25-6 に関する研究 (II) : 常温加工後の高温時効に及ぼす加工度および窒素の影響
スポンサーリンク
概要
- 論文の詳細を見る
The influence of the nitrogen (0.04∿0.16%), degree of working (0∿30%), and the solution-treatment temperature (1200°, 1250℃) on the high-temperature age-hardening of Timken 16-25-6 heat-resisting alloy were studied. The results were summarized as follows. (1) The hardness increased almost linearly by the cold working (0∿30%) but had little difference by the nitrogen content. (2) The age-hardening at 600℃ was not nearly influenced by the nitrogen content and the effect of the degree of working was somewhat greater than the effect of the solution-treatment temperature. In the case of aging at 700℃, the increase of hardness was remakable and the solution-treatment temperature was effective much greater than the degree of worklng, and the higher the solution-treatment temperature was, the more became the increase of hardness. On the contrary the higher the nitrogen content was, the smaller became the increase of hardness. The increase of hardness at 800℃ was smaller than that at 700℃ and the influence of nitrogen at 800℃ was similar to that at 700℃. (3) In regard to the influence of the degree of workeing on the increase of hardness, in the case of aging at 600℃, the increase of hardness decreased little according to increase of working, and in the case of aging at 700℃ the maximum increase was obtained by the working at 5∿10%. In the case of aging at 800℃, the increase of hardness decreased linearly according to increase of working and at the degree of working above 20% softening arose. (4) In the microstructure, the working accelerated the precipitation and the precipitate reaction became 4∿5 times by the 5% working. The greater the degree of working was, the more became the quantity of precipitates, and the more homogenious the distribution of precipitates. Generally the smaller the nitrogen content was, the faster became the coagulation of the precipitated particles. (5) In the tempering at 500∿1100℃ of cold worked (C∿50%) materials, the more the degree of working was, the lower became the temperature at which the maximum hardness obtained. In the case of tempering at 500∿1100℃ of 26% cold worked materials, the higher the nitrogen content was, the slower became the decrease of hardness.
- 社団法人日本鉄鋼協会の論文
- 1956-11-01
著者
関連論文
- 224 ころがり接触面の応力解析(疲れ・摩耗・残留応力, 性質, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- 50∿60kg/(mm)^2 級高張力鋼およびその溶接部の高温高圧水素による脆化
- 189 Cr-Ni-Mo 鋳鋼の熱処理と耐摩耗性について(鋳鋼・鋳鉄・被削性・疲労・その他, 性質, 日本鉄鋼協会第 77 回(春季)講演大会講演)
- 281 ボイラ管用 1Cr-1Mo-1/4V 鋼の性質について(高温強度, 性質, 日本鉄鋼協会 第 76 回(秋季)講演大会)
- A-302B 鋼の強度と靱性におよぼす焼準冷却速度の影響 : ASTM A-302B 厚鋼板の熱処理と機械的性質 I(講演論文特集号)
- 246 A-302B 鋼の強度と靱性におよぼす焼準冷却速度の影響 : ASTM A-302B 厚鋼板の熱処理と機械的性質 I(原子力・委員会報告講演・分析, 性質, 第 73 回(春季)講演大会講演論文集 (II))
- 55 耐熱鋼 Timken に及ぼす窒素の影響 (III) : 時効硬化に及ぼす常温加工の影響(日本鐵鋼協會第 45 回講演大會講演大要)
- 1Cr-1Mo-1/4V-B 耐熱鋼の高温特性と溶接性
- ボイラ主蒸気管用 1Cr-1Mo-1/4V 鋼の高温強度の改善
- 2 1/4 Cr-1Mo 耐熱鋼の高温強度の改善
- 耐熱合金 Timken 16-25-6 に関する研究 (III) : 焼戻における諸変化および析出物について
- 耐熱合金 Timken 16-25-6 に関する研究 (II) : 常温加工後の高温時効に及ぼす加工度および窒素の影響
- 耐熱合金 Timken 16-25-6 に関する研究 (I) : 高温時効に及ぼす溶体化処理および窒素の影響
- 63 耐熱鋼 Timken に及ぼす窒素の影響 (IV) : 焼戻に於ける析出による諸変化及び析出物に就て(日本鐵鋼協會第 48 回講演大會講演大要)