SiO_2-La_2O_3(CeO_2)-K_2O 系ガラスの溶出現象
スポンサーリンク
概要
- 論文の詳細を見る
The dissolving phenomenon of SiO_2-La_2O_3(CeO_2)-K_2O system glasses were studied in this paper. The fused glasses were powdered into particles of 35-60 meshes and lg of them were immersed in 50cc water of 303,323 and 343 K and agitated for 10,20,40 and 80 min.. Then the amount af K ion dissolved in water was measured by 0.1 or 0.01 N HCl. The results were as follows. (1) Log of amount of K ion dissolved in water was linear function of log of dissolving time and the reciprocal of dissolving temperature. (2) The amount of K ion dissolved in water depended on the concentration of SiO_2,rather than the concentration of K_2O. (3) The amount of K ion dissolved in water was more than the amount of Na ion and Li ion on same conditions.
- 山口大学の論文
著者
関連論文
- V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性(続報)
- V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性
- SiO_2(B_2O_3)-La_2O_3(CeO_2)-Li_2O 系ガラスの溶出現象
- B_2O_3-V_2O_5-CaO系ガラスより水中へ溶出するバナジウムイオンおよびカルシウムイオンの挙動
- B_2O_3-V_2O_5-CaO系ガラスの化学的耐久性
- SiO_2-B_2O_3-Na_2O系ガラスの化学的耐久性(第2報)
- SiO_2-Na_2O系ガラス生成反応 : Na源としてNaOHを用いた場合
- V_2O_5-P_2O_5-M_2O (M=Li, Na, K) 系ガラスの電気的性質
- B_2O_3-Fe_2O_3-R_2O (R : Na, K) 系ガラスの磁気的性質
- V_2O_5-P_2O_5 系および V_2O_5-P_2O_5-Na_2O 系ガラスの電気伝導
- SiO_2-La_2O_3(CeO_2)-K_2O 系ガラスの溶出現象
- SiO_2-La_2O_3 (C_eO_2)-Na_2O 系ガラスの溶出現象
- B_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの溶出現象
- B_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの磁気的性質
- B_2O_3-TiO_2-BaO系ガラスより水中へ溶出するチタンイオンおよびバリウムイオンの挙動
- ガラスより水中へ溶出するアルカリ・イオンの溶出量と溶出時間および溶出温度との関係式(第2報)
- ガラスより水中へ溶出する種々のイオンの溶出量と溶出時間および溶出温度との関係式(第2報)
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第2報) : SiO_2-Na_2O-TiO_2系
- SiO_2-B_2O_3-Na_2O系ガラスの化学的耐久性
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第1報) : SiO_2-Na_2-V_2O_5系
- B_2O_3-SiO_2-Na_2O系ガラスの化学的耐久性
- P_2O_5-Na_2O系およびP_2O_5-Na_2O-Al_2O_3系ガラスの化学的耐久性