B_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの磁気的性質
スポンサーリンク
概要
- 論文の詳細を見る
The magnetic properties of B_2O_3-Fe_2O_3-RO (R : Ba, Sr, Ca, Zn) system of glasses were studied in this paper. The glasses in this system were melted in electric furnace, about 1300℃, five hours. The melted glasses were powdered into particles of 80 meshes by agate mortar. The magnetic susceptibilities of the glasses were meaured by Gouy method. The results are as follows. 1) The magnetic susceptibilities are about 10-30×(10)^6(cm)^3g^<-1>, and are approximately equal to the susceptibility of Fe_2O_3 : 20.6×(10)^6(cm)^3g^<-1> (18℃) 2) The susceptibities are proportional to the contents of Fe_2O_3 mol in glasses and don't depend on the contents and species of other components in glasses.
- 山口大学の論文
著者
関連論文
- V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性(続報)
- V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性
- SiO_2(B_2O_3)-La_2O_3(CeO_2)-Li_2O 系ガラスの溶出現象
- B_2O_3-V_2O_5-CaO系ガラスより水中へ溶出するバナジウムイオンおよびカルシウムイオンの挙動
- B_2O_3-V_2O_5-CaO系ガラスの化学的耐久性
- SiO_2-B_2O_3-Na_2O系ガラスの化学的耐久性(第2報)
- SiO_2-Na_2O系ガラス生成反応 : Na源としてNaOHを用いた場合
- V_2O_5-P_2O_5-M_2O (M=Li, Na, K) 系ガラスの電気的性質
- B_2O_3-Fe_2O_3-R_2O (R : Na, K) 系ガラスの磁気的性質
- V_2O_5-P_2O_5 系および V_2O_5-P_2O_5-Na_2O 系ガラスの電気伝導
- SiO_2-La_2O_3(CeO_2)-K_2O 系ガラスの溶出現象
- SiO_2-La_2O_3 (C_eO_2)-Na_2O 系ガラスの溶出現象
- B_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの溶出現象
- B_2O_3-Fe_2O_3-RO (R=Ba, Sr, Ca, Zn) 系ガラスの磁気的性質
- B_2O_3-TiO_2-BaO系ガラスより水中へ溶出するチタンイオンおよびバリウムイオンの挙動
- ガラスより水中へ溶出するアルカリ・イオンの溶出量と溶出時間および溶出温度との関係式(第2報)
- ガラスより水中へ溶出する種々のイオンの溶出量と溶出時間および溶出温度との関係式(第2報)
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第2報) : SiO_2-Na_2O-TiO_2系
- SiO_2-B_2O_3-Na_2O系ガラスの化学的耐久性
- 遷移元素の酸化物を第3成分とするシリカ・ソーダ系ガラスの化学的耐久性(第1報) : SiO_2-Na_2-V_2O_5系
- B_2O_3-SiO_2-Na_2O系ガラスの化学的耐久性
- P_2O_5-Na_2O系およびP_2O_5-Na_2O-Al_2O_3系ガラスの化学的耐久性