V_2O_5-P_2O_5系およびV_2O_5-P_2O_5-BaO系ガラスの化学的耐久性

概要

論文の詳細を見る
The chemical durability for water of ten kinds glasses, i. e. 40VO_<2.5>- (60-x) PO_<2.5>-xBaO system and 60VO_<2.5>- (40-x) PO_<2.5>-xBaO system glasses (x=0,5,15,25,35) was examined, because of their interesting electrical properties, i. e. their low specific electrical resistances, fomer have 10^7-10^8 ohm. cm, latter 10^5-10^6 ohm. cm. The fused glasses were powdered into particles of 35-60 meshes and 2g of them were immersed in 50 cc water of 30℃, 50℃ and 70℃ under constant agitation of 10 min., 40 min., 80 min. and 160 min. respectively. Then the amounts of V, P and Ba dissolved in water were measured by chelatometric titration.The conclusions were as following. 1) The relations btween Log of the amounts of V, P and Ba dissolved in water and the reciprocal of absolute temperature of water were linear by theory, it was found that the theory was established approximately, though some results were not accord with it. 2) The amounts of V were decreased rapidly on the addition of BaO mol, but the amounts of P were not decreased as V.
山口大学の論文