Ruthenium Solubility and Dissolution Behavior in Molten Slag
スポンサーリンク
概要
- 論文の詳細を見る
- Japan Institute of Metalsの論文
- 2011-10-01
著者
-
Okabe Toru
Institute For Advanced Materials Processing Tohoku University
-
Morita Kazuki
Institute Of Industrial Science The University Of Tokyo
-
SHUTO Hiroshi
Institute of Industrial Science, The University of Tokyo
-
KABE Toru
Institute of Industrial Science, The University of Tokyo
-
Kabe Toru
Institute Of Industrial Science The University Of Tokyo
-
Shuto Hiroshi
Institute Of Industrial Science The University Of Tokyo
関連論文
- Semi-Continuous Production of Tantalum Powder by Electronically Mediated Reaction (EMR)
- Semi-continuous Production of Niobium Powder by Magnesiothermic Reduction of Nb_2O_5
- Production of Tantalum Powder by Magnesiothermic Reduction of Feed Preform
- Production of Niobium Powder by Preform Reduction Process Using Various Fluxes and Alloy Reductant
- Production of Niobium Powder by Magnesiothermic Reduction of Feed Preform
- Removal of Boron from Molten Silicon Using CaO-SiO_2 Based Slags
- Leaching of molydenum concentrate by electro-oxidation and recovery of molybdenum
- Electro-oxidation of molybdenum concentrate in sodium chloride solution
- Study on Leaching Process of Molybdenum Concentrate
- Recent Progress of EPM in Steelmaking, Casting, and Solidification Processing
- Behavior and State of Boron in CaO-SiO_2 Slags during Refining of Solar Grade Silicon
- Control of Si Crystal Growth during Solidification of Si-Al Melt
- Continuous Solidification of Si from Si-Al Melt under the Induction Heating
- Effects of 28GHz/2.45GHz Microwave Irradiation on the Crystallization of Blast Furnace Slag
- Activities of SiO_2 in Some CaO-Al_2O_3-SiO_2(-10%MgO) Melts with Low SiO_2 Contents at 1873K
- Evaluation of Hydrothermal Treatment to Immobilize Hexavalent Chromium in Wastewater Using Granulated Blast Furnace Slag
- Reaction Mechanisms of Blast Furnace Slag in Liquid and Vapor Dominated Hydrothermal Systems
- Effect of Microwave Irradiation on Hydrothermal Treatment of Blast Furnace Slag
- Surface Layer Formed by Selective Oxidation in High-Purity Copper-Titanium Binary Alloys
- High-Speed Titanium Production by Magnesiothermic Reduction of Titanium Trichloride
- Physicochemical Studies of Lithium Nitride in Molten LiC1-KC1
- Production of Metallic Vanadium by Preform Reduction Process
- New Method for Production of Solar-Grade Silicon by Subhalide Reduction
- Evaluation of Phase Diagrams for the Al_2O_3-CaO-SrO System by In-Situ Observation Using Confocal Laser Microscope
- Aluminum Deoxidation Equilibrium of Molten Iron-Aluminum Alloy with Wide Aluminum Composition Range at 1873K
- Platinum Recovery Using Calcium Vapor Treatment
- Direct Extraction and Recovery of Neodymium Metal from Magnet Scrap
- Production of Fine Tantalum Powder by Electrochemical Method
- Production of Titanium Powder by the Calciothermic Reduction of Titanium Concentrates or Ore Using the Preform Reduction Process
- Ruthenium Solubility and Dissolution Behavior in Molten Slag
- Thermodynamic Properties of the MgO-BO_, CaO-BO_, SiO_2-BO_, MgO-BO_-SiO_2 and CaO-BO_-SiO_2 Slag Systems at 1873K
- Erratum to “Thermodynamics of Si and Ti in Solid Fe at 1273 K” [ISIJ International 51 (2011), No 12, pp. 2002–2006]
- Thermodynamics of Si and Ti in Solid Fe at 1273 K
- Growth of $\beta$-FeSi2 Layers on Si(100) Substrates by Exchange Reaction between Si and Molten Salts
- Metallurgical characterization of high-copper amalgams : A brief history(Historia)