Removal of Boron from Molten Silicon Using CaO-SiO_2 Based Slags
スポンサーリンク
概要
- 論文の詳細を見る
The global shortage of solar grade silicon for the production of photovoltaic cells has motivated many researches on the refining of silicon, especially the refining of metallurgical-grade silicon. In order to obtain better control of the removal process of boron from molten silicon using silicate slags, precise thermodynamic data are required. In the present study the partition ratio of boron (LB) between the slag and silicon phases and the activity coefficient of boron oxide in CaO–SiO2, CaO–SiO2–25%CaF2, and CaO–SiO2–40%CaF2 slags were evaluated at 1823 K. The activity coefficient of BO1.5 was investigated for slags of CaO/SiO2 ratio varying from 0.3–7.0; further, the borate capacity of the slag is defined in this study as:<center><a href="http://ess.jstage.jst.go.jp/preview/article/isijinternational/49/6/49_783/_appendix/1">[Equation]</a></center>The addition of Na2O to CaO–SiO2 slags was found to increase the partition ratio of boron between the slag and the silicon phase.
- 2009-06-15
著者
-
Morita Kazuki
Institute Of Industrial Science The University Of Tokyo
-
Teixeira Leandro
Institute Of Industrial Science The University Of Tokyo
関連論文
- Removal of Boron from Molten Silicon Using CaO-SiO_2 Based Slags
- Recent Progress of EPM in Steelmaking, Casting, and Solidification Processing
- Behavior and State of Boron in CaO-SiO_2 Slags during Refining of Solar Grade Silicon
- Control of Si Crystal Growth during Solidification of Si-Al Melt
- Continuous Solidification of Si from Si-Al Melt under the Induction Heating
- Effects of 28GHz/2.45GHz Microwave Irradiation on the Crystallization of Blast Furnace Slag
- Activities of SiO_2 in Some CaO-Al_2O_3-SiO_2(-10%MgO) Melts with Low SiO_2 Contents at 1873K
- Evaluation of Hydrothermal Treatment to Immobilize Hexavalent Chromium in Wastewater Using Granulated Blast Furnace Slag
- Reaction Mechanisms of Blast Furnace Slag in Liquid and Vapor Dominated Hydrothermal Systems
- Effect of Microwave Irradiation on Hydrothermal Treatment of Blast Furnace Slag
- Evaluation of Phase Diagrams for the Al_2O_3-CaO-SrO System by In-Situ Observation Using Confocal Laser Microscope
- Aluminum Deoxidation Equilibrium of Molten Iron-Aluminum Alloy with Wide Aluminum Composition Range at 1873K
- Ruthenium Solubility and Dissolution Behavior in Molten Slag
- Thermodynamic Properties of the MgO-BO_, CaO-BO_, SiO_2-BO_, MgO-BO_-SiO_2 and CaO-BO_-SiO_2 Slag Systems at 1873K
- Erratum to “Thermodynamics of Si and Ti in Solid Fe at 1273 K” [ISIJ International 51 (2011), No 12, pp. 2002–2006]
- Thermodynamics of Si and Ti in Solid Fe at 1273 K
- Growth of $\beta$-FeSi2 Layers on Si(100) Substrates by Exchange Reaction between Si and Molten Salts