Evaluation of Hydrothermal Treatment to Immobilize Hexavalent Chromium in Wastewater Using Granulated Blast Furnace Slag
スポンサーリンク
概要
- 論文の詳細を見る
The immobilization of hexavalent chromium in wastewater using blast furnace slag as the immobilizing agent was investigated by using hydrothermal treatment. The results showed that immobilization was not attained without a hydrothermal treatment, while hexavalent chromium in solution could be immobilized through the process of hydrothermal treatment with the blast furnace slag at 250°C for 18 h. In particular, the reducing condition was attributed to the presence of sulfur in the blast furnace slag, which indicated that the sulfur could plays key role in the immobilization of hexavalent chromium in the present study. In addition, the leaching test was carried out to evaluate the level of immobilization of hexavalent chromium in the products after the hydrothermal treatment, and it was found that the degree of immobilization was very high. Based on the results obtained in the present study, the immobilization mechanism of the hydrothermal treatment of blast furnace slag in wastewater was elucidated.
- 社団法人 日本鉄鋼協会の論文
- 2008-09-15
著者
-
Morita Kazuki
Institute Of Industrial Science The University Of Tokyo
-
Tae Soon-jae
Institute Of Industrial Science The University Of Tokyo
関連論文
- Removal of Boron from Molten Silicon Using CaO-SiO_2 Based Slags
- Recent Progress of EPM in Steelmaking, Casting, and Solidification Processing
- Behavior and State of Boron in CaO-SiO_2 Slags during Refining of Solar Grade Silicon
- Control of Si Crystal Growth during Solidification of Si-Al Melt
- Continuous Solidification of Si from Si-Al Melt under the Induction Heating
- Effects of 28GHz/2.45GHz Microwave Irradiation on the Crystallization of Blast Furnace Slag
- Activities of SiO_2 in Some CaO-Al_2O_3-SiO_2(-10%MgO) Melts with Low SiO_2 Contents at 1873K
- Evaluation of Hydrothermal Treatment to Immobilize Hexavalent Chromium in Wastewater Using Granulated Blast Furnace Slag
- Reaction Mechanisms of Blast Furnace Slag in Liquid and Vapor Dominated Hydrothermal Systems
- Effect of Microwave Irradiation on Hydrothermal Treatment of Blast Furnace Slag
- Evaluation of Phase Diagrams for the Al_2O_3-CaO-SrO System by In-Situ Observation Using Confocal Laser Microscope
- Aluminum Deoxidation Equilibrium of Molten Iron-Aluminum Alloy with Wide Aluminum Composition Range at 1873K
- Ruthenium Solubility and Dissolution Behavior in Molten Slag
- Thermodynamic Properties of the MgO-BO_, CaO-BO_, SiO_2-BO_, MgO-BO_-SiO_2 and CaO-BO_-SiO_2 Slag Systems at 1873K
- Erratum to “Thermodynamics of Si and Ti in Solid Fe at 1273 K” [ISIJ International 51 (2011), No 12, pp. 2002–2006]
- Thermodynamics of Si and Ti in Solid Fe at 1273 K
- Growth of $\beta$-FeSi2 Layers on Si(100) Substrates by Exchange Reaction between Si and Molten Salts