Crystallization Behaviors of Mold Fluxes Containing Li_2O Using Single Hot Thermocouple Technique
スポンサーリンク
概要
- 論文の詳細を見る
Minor addition of Li2O (<2 mass%) can significantly alter the melting temperature and viscosity of a mold flux. However, the crystallization tendency of mold fluxes containing Li2O more than 2 mass% hasnt been understood. In this paper, single hot thermocouple technique, X-ray diffraction, and Back Scattered Electron (BSE) were employed to investigate the crystallization behavior concerned with CCT and TTT diagrams of mold fluxes containing high content of Li2O.The critical cooling rate and crystallization rate of samples were increased with the addition of Li2O, whether there is Na2O or not. But the incubation time was reduced obviously with Li2O more than 6 mass% in mold fluxes. The critical cooling rate and incubation time of NL1.5 sample (Na2O=8 mass%, Li2O=1.5 mass%) were close to those of L7 sample (Na2O=0 mass%, Li2O=7 mass%). Moreover, there is no difference in the crystal phase of the two samples, and the crystal phases precipitated at high temperature and low temperature were respectively Ca2(SiO4) and Ca4Si2O7F2. Li-cuspidine was promoted to precipitate when the basicity of the sample was increased. The small, dense grains of cuspidine were observed in NL1.5 sample, and the thickness of slag film was 0.4 mm more than that of L7 sample. The heat flux of NL1.5 sample measured was 10% less than that of L7 sample, as expected. Therefore, high content of Li2O can be substituted by the combination of Na2O and minor of Li2O, as is the composition in the commercial mold fluxes.
- 社団法人 日本鉄鋼協会の論文
- 2009-06-15
著者
-
Wen Guanghua
Department of Materials Science and Engineering, Carnegie Mellon University
-
Tang Ping
Department of Materials Science and Engineering, Chongqing University
-
LIU Hui
Department of Pharmacognosy, Graduate School of Biomedical Sciences, Hiroshima University
-
Wen Guanghua
Department Of Metallurgy College Of Materials Science And Engineering Chongqing University
-
Liu Hui
Department Of Applied Mathematics Hebei University Of Technology
-
Tang Ping
Department Of Metallurgy College Of Materials Science And Engineering Chongqing University
-
Liu Hui
Department Of Metallurgy College Of Materials Science And Engineering Chongqing University
-
LIU Hui
Department of Anesthesiology, West China Second University Hospital, Sichuan University
関連論文
- The Influence of Al2O3/SiO2 Ratio on the Viscosity of Mold Fluxes
- Bridelioside, a new lignan glycoside from Bridelia glauca Bl. f. balansae (Tucht.) Hatusima
- Development of Fluoride-free Mold Powders for Peritectic Steel Slab Casting
- The Influence of Al_2O_3/SiO_2 Ratio in the Viscosity of Mold Fluxes
- Crystallization Behaviors of Mold Fluxes Containing Li_2O Using Single Hot Thermocouple Technique
- Predictive value of MMP-7 expression for response to chemotherapy and survival in patients with non-small cell lung cancer
- ^C, ^O, ^Si NMR Spectra and Stabilization of Silylated Ketenes and Bisketenes
- A subset of breast cancer predisposes to brain metastasis
- On the existence of nonnegative radial solutions for elliptic system
- Validation of the Simplified Chinese Version of the Oswestry Disability Index
- Zero and Controllable Linewidth Enhancement Factor in p-Doped 1.3 μm Quantum Dot Lasers
- Antitumor activity and drug interactions of proteasome inhibitor Bortezomib in human high-risk myelodysplastic syndrome cells
- The Development of Classically and Alternatively Activated Macrophages Has Different Effects on The Varied Stages of Radiation-induced Pulmonary Injury in Mice
- Weight of the CURB-65 Criteria for Community-Acquired Pneumonia in a Very Low-Mortality-Rate Setting
- Neoadjuvant chemotherapy followed by radical surgery and reconstruction of the vagina in a patient with stage II primary vaginal squamous carcinoma
- Survey of labor epidural analgesia and patient education for women in southwest China
- Lung Squamous Cell Carcinoma in Pulmonary Alveolar Proteinosis