Refinement of As-cast Austenite Microstructure in S45C Steel by Titanium Addition
スポンサーリンク
概要
- 論文の詳細を見る
The effect of Ti addition on as-cast austenite (γ) structure of S45C steel has been investigated. The as-cast γ structure without the Ti addition consists of coarse columnar grains. The Ti addition leads to formation of equiaxed γ-grains and also grain refinement of the γ structure. Fully equiaxed and very fine γ-grain structure forms in a limited range of Ti addition of 0.13 to 0.17 wt%. The thermodynamic calculation of phase diagram showed that Ti carbonitride crystallizes as a primary phase in this composition range. The formation of the very fine equiaxed γ-grain structure originates from the columnar-to-equiaxed transition (CET) in δ-dendrite solidification induced by the primary Ti carbonitride particles. These particles act as the nucleation sites of the equiaxed δ-dendrite. The experimental results are suggestive of existence of finer Ti carbonitride particles retarding the grain growth of γ-phase after the peritectic transformation, which leads to the refinement of the as-cast γ structure.
- 社団法人 日本鉄鋼協会の論文
- 2008-10-15
著者
-
Matsuura Kiyotaka
Division Of Materials Science And Engineering Hokkaido University
-
Ohno Munekazu
Division Of Materials Science And Engineering Graduate School Of Engineering Hokkaido University
-
Ohno Munekazu
Division Of Material Science And Engineering Graduate School Of Engineering Hokkaido University
-
Matsuura Kiyotaka
Division Of Material Science And Engineering Hokkaido University
-
Matsuura Kiyotaka
Division Of Materials Science And Engineering Graduate School Of Engineering Hokkaido University
関連論文
- Theoretical Investigation of Coarsening Process of L1_0-Ordered Domain Based on Phase Field Method and Cluster Variation Method
- Disorder-L1_0 Transition Investigated by Phase Field Method with CVM Local Free Energy
- Powder-Metallurgical Process for Producing Metallic Microchannel Devices
- Freeform Fabrication of Titanium by 3D Micro Welding(Materials, Metallurgy & Weldability)
- Padding, Welding and Freeform Fabrication of Nickel Aluminide Intermetallic Compound by Reactive Rapid Prototyping Process
- Padding, Welding and Freeform Fabrication of Nickel Aluminide Intermetallic Compound by Reactive Rapid Prototyping Process
- Transient Behavior of a Stress-Strain Curve within Cottrell-Stokes Law
- Effect of Niobium on the Formation of Microstructure and Grain Boundary in Fe-Nb and Fe-C-Nb Alloys
- Solidification Behavior of Iron-Niobium and Iron-Carbon-Niobium alloys
- Thermodynamic Calculation of Phase Equilibria in As-Fe-In Ternary System Based on CALPHAD Approach