Microstructure of Martensite/Bainite Dual-phase Grey Cast Iron and Its Strengthening Mechanism
スポンサーリンク
概要
- 論文の詳細を見る
By a process of combinations of microalloying with Ni, Mo and other elements, cast chilled by metal-mold and special heat-treatment, A martensite/bainite (M/B) dual-phase grey cast iron was fabricated. Quenching into oil after austenization at 900°C for 2 h, the hardness of the sample was above HRC 48. The microstructures of all samples were characterized by optical metallography or X-ray diffraction. The final microstructure was composed of M/B dual-phase and retained austenite. There were some “white-bright zone” composed of few high-carbon martensite plates and retained austenite, full of Mn and Mo elements, concentrating on the boundaries of eutectic cells. The nucleation site and mechanism of bainite were studied by short oil-quenching for 5 s after austenization at 860°C for 2 h. The result showed bainite first nucleated at interface between flake graphite and austenite, and austenite along the direction of flake graphite sharp corner was also tend to transform into bainite. The second site easy for bainite nucleation was the boundary of austenite, also the boundary of “white-bright zone”. Strengthening mechanism of M/B dual-phase to this grey cast iron was studied by using pressing-in method to press round head into the surface of corrosive M/B dual-phase grey cast iron. The initiation and extension of cracks were observed through SEM. The result showed that M/B dual-phase could effectively strengthen graphite–matrix interface and restrain cracks extension, tips of high-carbon martensites in “white-bright zone” were another site prone to initiate cracks under pressure. For lake of phase–phase interfaces, the cracks would extend straightly until to the whole interface of “white-bright zone” and matrix.
- 社団法人 日本鉄鋼協会の論文
- 2007-12-15
著者
-
Wang Qiang
Northeastern Univ.
-
Wang Qiang
Department Of Anesthesiology Plastic Surgery Hospital Chinese Academy Of Medical Sciences And Peking
-
XING Junbai
Department of Materials Science and Engineering, Jilin University at Nanling Campus
-
CHANG Jinpeng
Department of Materials Science and Engineering, Jilin University at Nanling Campus
-
Xing Junbai
Department Of Materials Science And Engineering Jilin University At Nanling Campus
-
Chang Jinpeng
Department Of Materials Science And Engineering Jilin University At Nanling Campus
関連論文
- Erratum: Intensification of Bubble Disintegration and Dispersion by Mechanical Stirring in Gas Injection Refining[ISIJ. Int. 49(1): 17-23 (2009)]
- Identification of Aluminum Species in an Aluminum-accumulating Plant, Hydrangea (Hydrangea macrophylla), by Electrospray Ionization Mass Spectrometry
- FOXP3 is a homo-oligomer and a component of a supramolecular regulatory complex disabled in the human XLAAD/IPEX autoimmune disease
- A Channel Equalization Technique on a Time Division Duplex CDMA/TDMA System for Wireless Multimedia Networks
- A Transmission Power Control Technique on a TDD-CDMA/TDMA System for Wireless Multimedia Networks
- A Wireless Multimedia Network on a Time Division Duplex CDMA/TDMA
- Fabrication and Characterization of 3-DOF Soft-Contact Tactile Sensor Utilizing 3-DOF Micro Force Moment Sensor
- Laparoscopic Management of Recurrent Adhesive Small-Bowel Obstruction : Long-Term Follow-Up
- Electromagnetic Field Distribution in Two-section Slitless Mold for Soft-contact Electromagnetic Continuous Casting
- 20-P2-CJK15 Evaluation and Analysis of the amendment of prescribing information for ceftriaxone base on the interaction with calcium-containing products
- Determination of scopoletin in rat plasma by high performance liquid chromatographic method with UV detection and its application to a pharmacokinetic study
- Effects of Uniform and Gradient High Magnetic Fields on Gravity Segregation in Aluminum Alloys
- Prediction of Solidification Microstructure and Columnar-to-equiaxed Transition of Al-Si Alloy by Two-dimensional Cellular Automaton with "Decentred Square" Growth Algorithm
- Intensification of Bubble Disintegration and Dispersion by Mechanical Stirring in Gas Injection Refining
- In-Situ Fabrication of Bi/BiMn-BiMn-Mn Graded Materials by High Magnetic Field Gradients
- Solidified Structure Control of Metallic Materials by Static High Magnetic Fields
- Analysis of an Automatic Steel-teeming Method Using Electromagnetic Induction Heating in Slide Gate System
- Increased Expression of Annexin A1 Is Correlated with K-Ras Mutation in Colorectal Cancer
- Comments on use of a Parker Flex-Tip tube^【○!R】 to facilitate intubation with the Pentax-AWS^【○!R】
- Can 8% lidocaine spray 10min prior to endotracheal intubation reduce the incidence of postoperative sore throat?
- Microstructure of Martensite/Bainite Dual-phase Grey Cast Iron and Its Strengthening Mechanism
- Generation of Compression Waves by Simultaneously Imposing a Static Magnetic Field and an Alternating Current and Its Use for Refinement of Solidified Structure
- Non-Contact Generation of Intense Compression Waves in a Molten Metal by Using a High Magnetic Field
- Cellular prion protein promotes glucose uptake through the Fyn-HIF-2α-Glut1 pathway to support colorectal cancer cell survival
- Effect of Heat Treatment on Microstructure and Mechanical Properties of Ti-alloyed Hypereutectic High Chromium Cast Iron
- Effect of Cooling Rate and Ti Addition on the Microstructure and Mechanical Properties in As-cast Condition of Hypereutectic High Chromium Cast Irons
- Effect of Heat Treatment on Microstructure and Mechanical Properties of Ti-alloyed Hypereutectic High Chromium Cast Iron
- Randomized, multicenter, double-blind, and placebo-controlled trial using topical recombinant human acidic fibroblast growth factor for deep partial-thickness burns and skin graft donor site