Isothermal Precipitation Behavior of Copper Sulfide in Ultra Low Carbon Steel
スポンサーリンク
概要
- 論文の詳細を見る
Copper and sulfur are typical residual elements or impurity elements in steel. Sufficient removal of them during steelmaking process is difficult for copper and costly for sulfur. Utilization of copper and sulfur in steel, especially in steel scrap, has been an important issue for a long period for metallurgists.Copper and sulfur may combine to form a copper sulfide, which may provide a prospect to avoid the detrimental effects of copper and sulfur in steel. Unfortunately the formation mechanism of a copper sulfide in steel has not been completely clarified so far. In the present paper, solution treatment of samples containing copper and sulfur are firstly performed at 1623 K for 2.7×103 s followed by quenching into water. The samples are then isothermally heat-treated at 673 K, 873 K, 1073 K, 1273 K and 1373 K for different time followed by quenching into water again. The size, morphology, constituent and crystallography of sulfide precipitates in these samples are investigated by SEM and TEM equipped with EDS. Fine copper sulfides (less than 100 nm) are observed to co-exist with silicon oxide in samples even isothermally heat-treated at 1373 K for 1.44×104 s; Film-like copper sulfides are generally observed to co-exist with iron sulfide in all samples; Plate-like copper sulfides are observed especially in sample isothermally heat-treated at 1073 K for 1.44×104 s. The formation mechanisms of these copper sulfides have been discussed in detail.
- 社団法人 日本鉄鋼協会の論文
- 2007-11-15
著者
-
KUWABARA Mamoru
Graduate School of Engineering, Nagoya University
-
LIU Zhongzhu
Graduate School of Engineering, Nagoya University
-
Liu Zhongzhu
Graduate School Of Engineering Nagoya University
-
Kuwabara Mamoru
Graduate School Of Engineering Nagoya University
-
IWATA Yosihisa
Graduate School of Engineering, Nagoya University
-
Iwata Yosihisa
Graduate School Of Engineering Nagoya University
-
Liu Zhongzhu
Graduate School Of Engineering Nagoya Univ.
関連論文
- Acoustic Cavitation-based Processing of Materials
- Effect of Nano-Scale Copper Sulfide Precipitation on Mechanical Properties and Microstructure of Rapidly Solidified Steel with Tramp Copper Element
- "In-situ" Observation of the δ/γ Phase Transformation on the Surface of Low Carbon Steel Containing Phosphorus at Various Cooling Rates
- Morphology Control of Copper Sulfide in Strip Casting of Low Carbon Steel
- In Situ Observation of Aluminothermic Reduction of MgO with High Temperature Optical Microscope
- Improvement on Desulfurization Efficiency of Molten Iron with Magnesium Vapor Produced In-situ by Aluminothermic Reduction of Magnesium Oxide
- Nucleation of Acicular Ferrite on Sulfide Inclusion during Rapid Solidification of Low Carbon Steel
- Interaction between Phosphorus Micro-Segregation and Sulfide Precipitation in Rapidly Solidified Steel-Utilization of Impurity Elements in Scrap Steel
- Effect of Phosphorus on Sulfide Precipitation in Strip Casting Low Carbon Steel
- Crystallography and Precipitation Kinetics of Copper Sulfide in Strip Casting Low Carbon Steel
- Precipitation of Copper Sulfides and their Effects on Mechanical Properties in Strip Casting Low Carbon Steel
- Effect of Nano-Scale Copper Sulfide Particles on the Yield Strength and Work Hardening Ability in Strip Casting Low Carbon Steel
- Simultaneous Desulfurization and Deoxidation of Molten Steel with in Situ Produced Magnesium Vapor
- Nucleation and Growth of Alumina Inclusion in Early Stages of Deoxidation : Numerical Modeling
- Isothermal Precipitation Behavior of Copper Sulfide in Ultra Low Carbon Steel