Reaction between Magnesia-Chrome Brick/Slag Interface by Electric Furnace Static Slag Corrosion Test
スポンサーリンク
概要
- 論文の詳細を見る
- Japan Institute of Metalsの論文
- 2008-01-01
著者
-
HON Min-Hsiung
Department of Materials Science and Engineering, National Cheng Kung University
-
Hon Min-hsiung
Department Of Materials Engineering National Cheng Kung University
-
Wang Moo-chin
Faculty Of Fragrance And Cosmetics Kaohsiung Medical University
-
HSU Chia-Chan
Department of Materials Science and Engineering, National Cheng Kung University
-
Hsu Chia-chan
Department Of Materials Science And Engineering National Cheng Kung University
関連論文
- Effects of Calcination and Hot-Pressing Temperatures of Magnesium Fluoride Powder on Its Optical Property
- 酸素雰囲気下におけるLiNiO_2のペチーニ法合成メカニズム
- クエン酸ゲル法で合成されたLiMn_2O_4ナノ粒子の電気化学的特性
- クエン酸ゲルプロセスによって合成したLiMn_2O_4粉末の相安定性と形態に及ぼす熱処理温度と雰囲気の影響
- The Dependence of Properties of Alumina-Zirconia-Graphite Refractories on Particle Size Distribution by Furnas Model
- アルミナ-ジルコニア-グラファイト系耐火物の特性に及ぼす粒度分布の影響
- Fabrication and characteristics of the low resistivity p-type ZnO thin films by nitrogen ion implantation
- Debinding Process of Fe-6Ni-4Cu Compact Fabricated by Metal Injection Modeling
- Effect of Processing on Removal of Hydroxyl Absorption Bands in Li_20-Ca0 -A1_20_3-Ge0_2 Glass
- Dielectric Properties and Leakage Current Characterization of the Ba(Sn_xTi_)O_3 Thin Films Prepared by Radio Frequency Magnetron Sputtering
- Effect of Thermal Treatment on the Intermetallic Compounds Formed at Sn-9Zn-1.5Ag-xBi (x = 0 and 1) Lead-Free Solder/Cu Interface
- Thermal Characteristics and Intermetallic Compounds Formed at Sn-9Zn-0.5Ag/Cu Interface
- Growth of ZnO Single Crystals by Annealing Sol-Gel-derived Films with PDMS Pre-pressing
- ワイブル統計で評価したアルミナの射出成形におけるプロセッシング安定性に及ぼす固相量の影響
- Reaction between Magnesia-Chrome Brick/Slag Interface by Electric Furnace Static Slag Corrosion Test
- Si_3N_4とTiCセラミックスの反応機構
- Characteristics and Optical Properties of Ni Nanograins Reduced on TiO2 Film
- A Three-Dimensional Nanostructure Consisting of Hollow TiO2 Spheres Fabricated by Atomic Layer Deposition