密度汎関数法及びラマンスペクトル法を用いたSnCl_2-EMIC常温型溶融塩浴の構造解析
スポンサーリンク
概要
著者
-
凌 国平
College of Materials Science and Chemical Engineering, Zhejiang University
-
宇井 幸一
Department of Industrial and Engineering Chemistry, Faculty of Science and Technology, Tokyo Univers
-
小浦 延幸
Department of Industrial and Engineering Chemistry, Faculty of Science and Technology, Tokyo Univers
-
小浦 延幸
Faculty Of Science And Technology Tokyo University Of Science
-
宇井 幸一
Faculty Of Science And Technology Tokyo University Of Science
-
中井 涼
Department Of Industrial And Engineering Chemistry Faculty Of Science And Technology Tokyo Universit
-
宇井 幸一
Department Of Frontier Materials And Function Engineering Graduate School Of Engineering Iwate Unive
-
松澤 秀則
Department of Life and Environmental Sciences, Faculty of Engineering, Chiba Institute of Technology
-
凌 国平
Department of Material Science & Engineering, Zhejiang University
-
小浦 延幸
東理大・理工
-
松澤 秀則
千葉工大工
-
凌 国平
College Of Materials Science And Chemical Engineering Zhejiang University
関連論文
- 23aGH-10 圧力効果と鉄系超伝導体Sr_2VFeAsO_3の^As-NMR測定(23aGH Fe(Se,Te),新規物質等(置換効果,分光等),領域8(強相関系:高温超伝導,強相関f電子系など))
- ルイス塩基性NbCl_5-SnCl_2-EMIC浴からのNb_3Sn合金膜の電析
- 5V級Li二次電池正極活物質LiMn_Ni_O_4の合成条件による物性, 結晶構造と電極特性の関係
- 高温超伝導体の低温における臨界電流特性の比較
- 定比組成Bi(Pb)2223線材の高T_c化
- Premix-PICT 拡散法で作製したMgB_2超伝導バルク体の臨界電流特性に及ぼす微細組織の影響
- c軸配向高密度MgB_2バルクの開発
- 希土類系高温超伝導体の磁気異方性と三軸磁場配向
- 磁気配向法によるc軸配向MgB_2バルクの作製
- 結晶成長方位を変えたY123バルクの特徴