Numerical Estimation of the Effect of the Magnetic Field Application on the Motion of Inclusion in Continuous Casting of Steel
スポンサーリンク
概要
- 論文の詳細を見る
Numerical estimation has been conducted to analyze the motion of inclusion considering the effects of argon gas injection and magnetic field application in the continuous casting of slab. The fluid velocity field was obtained by solving the Navier-Stokes equations with electromagnetic force, and the trajectories of inclusion particles are calculated based on the computed velocity field. A reasonable agreement between numerical and experimental trajectory for single sphere was obtained using the water model. The movements of particles are traced in cases with and without the magnetic field and argon gas injection. The results show that some particles after spiral movements re-enter the jet zone of molten steel, and then enter the opposite circulation zone. Inclusions in the upper circulation zone are easily removed. Argon gas injection increases the removal rate of inclusions. The spiral trajectories of inclusion particles disappear when the magnetic field is applied, and the particle velocities decrease significantly. The argon gas injection and magnetic field application are effective for the control of the inclusions.
- 社団法人 日本鉄鋼協会の論文
- 2003-06-15
著者
-
Tsukihashi Fumitaka
Department Of Advanced Materials Graduate School Of Frontier Science The University Of Tokyo
-
Li Baokuan
Department Of Thermal Engineering School Of Materials And Metallurgy Northeastern University
-
Tsukihashi Fumitaka
Department Of Advanced Materials Graduate School Of Frontier Sciences The University Of Tokyo
-
Tsukihashi Fumitaka
Department Of Advanced Material Science The University Of Tokyo
関連論文
- Temperature Coefficient of Surface Tension and their Comparison for Molten tin at Different Oxygen Potentials of the Measured Conditions
- The Effect of Na_2O and Al_2O_3 on Dephosphorization of Molten Steel by High Basicity MgO Saturated CaO-FeO_x-SiO_2 Slag
- Wettability and Interfacial Permeability between Prereduced Ilmenite and Molten Pig Iron
- Dissolution Behavior of Solid 5CaO・SiO_2・P_2O_5 in CaO-SiO_2-FeO_x Slag
- Condensation of P_2O_5 at the Interface between 2CaO・SiO_2 and CaO-SiO_2-FeO_x-P_2O_5 Slag
- Effect of Simultaneous Addition of Al_2O_3 and MgO on the Liquidus of the CaO-SiO_2-FeO_x System with Various Oxygen Partial Pressures at 1573K
- Reduction Extraction Kinetics of Titania and Iron from an Ilmenite by H_2-Ar Gas Mixtures
- Removal of Antimony from Liquid Copper by Using CuCl-Na_2CO_3 Fluxes at 1423K
- Mechanisms of Oxidation and Vaporization of Antimony from Liquid Copper with CuCl-CaO Fluxes
- Chlorination Kinetics of ZnFe_2O_4 with Ar-Cl_2-O_2 Gas