溶融塩ホウ化処理によるTiAlの耐酸化性改善(エコマテリアルの開発)(Part-2. 鉄鋼業と循環型社会)(<特集>鉄の技術と文化および循環型社会)

概要

論文の詳細を見る
The high temperature oxidation resistance of high specific strength intermetallic compound TiAl was improved by boronizing using chrolide and boride molten salt The molten salt process has some remarkable characteristics as follows, 1) very simple process, 2) the atomosphere doesn't effect on the chemical reaction in the liquid, 3) specimen is fully dipped into the treatment liquid TiB_2 and Al_3Ti layers were produced on the surface of TiAl by this process The dense and protective Al_20_3 phase was observed on the Al_3Ti layer The boronized TiAl was investigated in continuous and cyclic oxidation test at 1173K and 1123K The mass gain due to oxidation of TiAl decreased by boronizing, where no pealing was observed during oxidation test
社団法人日本鉄鋼協会の論文
2005-01-01