Mechanical and Thermal Properties of Compression Molded Poly (acrylic acid) Salts with Multivalent Metal Ions
スポンサーリンク
概要
- 論文の詳細を見る
Films of zinc, calcium and aluminum salts of poly (acrylic acid) (PAA) were prepared from their powdery salts by compression molding at 190_??_200°C, 600MPa for 0.5hr and their mechanical and thermal properties were investigated. From the results of the dynamic mechanical thermal analysis the storage modulus of each PAA salts exhibited about 20GPa at room temperature because of highly intermolecular crosslinking of PAA by metal ions. Modulus of PAA calcium salt was 7GPa even at 400°C, while modulus of zinc salt and aluminum salt of PAA decreased abruptly above 200°C. This decrease of modulus was attributed to the abrupt elimination of H2O, which coordinated to metal ions, from specimens at high temperature.
- Sen'i Gakkaishi. 55(11):522-527 (1999)の論文
- 1999-11-10
著者
-
OHKOSHI Yutaka
Faculty of Textile Science of Technology, Shinshu University
-
奈倉 正宣
信州大学繊維学部
-
GOTOH Yasuo
Faculty of Textile Science and Technology, Shinshu University
-
NAGURA Masanobu
Faculty of Textile Science and Technology, Shinshu University
-
Gotoh Yasuo
Faculty Of Textile Science And Technology Shinshu University
-
奈倉 正宣
Faculty Of Textile Science And Technology Shinshu University
-
Ohkoshi Y
Faculty Of Textile Science And Technology Shinshu University
-
Ohkoshi Yutaka
Faculty Of Textile Science And Technology Shinshu University
-
Nagura Masanobu
Faculty Of Textile Science And Technology Shinshu University
-
後藤 康夫
Faculty of Textile Science and Technology, Shinshu University
-
大越 豊
Faculty of Textile Science and Technology, Shinshu University
関連論文
- 実用的な高含水セリシンフィルムの作製とその物性
- セリシン蚕から得られたセリシンの構造と物性
- Initial structure development in the CO2 laser-heated drawing of poly(trimethylene terephthalate) fiber
- Thermoplastic Polyurethane Ultrafine Fiber Web Fabricated by Laser Electrospinning
- 溶融混練によるカルボキシル基含有ポリマー : 酸化銅複合体の作製およびその硫化処理による近赤外線吸収特性の発現
- ヒーター加熱とレーザー照射加熱の併用によるポリL乳酸 / ε-カプロラクトン共重合体モノフィラメントの延伸
- 高分子-ヨウ素錯体を前駆体としたナイロン6/ヨウ化銀コンポジット繊維の創製
- ポリエチレンテレフタレート繊維のレーザー延伸時におけるエネルギー収支
- セリシン蚕セリシンより得られた高分子量セリシンの構造と物性
- 炭酸ガスレーザー加熱延伸されたポリエチレンテレフタレート繊維の分子鎖配向挙動と結晶化度
- 炭酸ガスレーザー加熱延伸法により作製されたポリエチレンテレフタレート繊維の力学的性質
- 炭酸ガスレーザー加熱延伸法により作製されたポリエチレンテレフタレート繊維の構造
- アシル化キトサンの構造と物性
- ポリビニルアルコール/セリシンブレンド膜の構造と物性
- チタンイオンにより架橋されたメタクリル系アイオノマーの光吸収特性
- 熱可塑性ポリウレタン纎維の繰り返し伸長回復による力学的性質および相分離構造の変化
- ポリエーテルエーテルケトンの溶融紡糸線上での冷却挙動
- ポリメタクリル酸メチル中におけるリン酸エステル-2価銅イオン錯体の構造
- Development of a fiber structure in poly(vinylidene fluoride) by a CO_2 laser-heated drawing process
- The Effect of Applied Voltage and Laser Power on the Molecular Orientation of Laser-Electrospun Poly(ethylene terephthalate) Fibers
- Electrospinning of poly (ether sulfone) and evaluation of the filtration efficiency
- Mechanical Properties of Poly(ethylene terephthalate) Fiber Produced by Conjugate Melt Spinning with Polystyrene and CO2 Laser-Heated Drawing (特集 高強度繊維)
- ポリスチレンスルホン酸ナトリウムを溶出させることにより調製したポリビニルアルコールハイドロゲルの表面構造と細胞付着・増殖抑制効果
- Ultra-Fine Fibers Produced by Laser-Electrospinning
- 教養教育としての物質科学(講義室)
- Initial stage of fiber structure development in the continuous drawing of poly(ethylene terephthalate)
- Initial Stage of Fiber Structure Development in the Continuous Drawing of Poly(ethylene terephthalate)
- Conductivity and structure of a polyamide/silver iodide nanocomposite
- Carbon fiber from natural biopolymer Bombyx mori silk fibroin with iodine treatment
- Poly(ethylene terephthalate) nanofibers made by sea-island-type conjugated melt spinning and laser-heated flow drawing
- ヒト毛髪タンパク質と絹フィブロインから成る複合フィルムの作製と性質
- Drawing behavior and characteristics of laser-drawn polypropylene fibers
- Hydration in a new semiaromatic polyamide observed by humidity-controlled dynamic viscoelastometry and X-ray diffraction
- Online wide-angle X-ray diffraction/small-angle X-ray scattering measurements for the CO2-laser-heated drawing of poly(ethylene terephthalate) fiber
- Preparation and Viscoelastic Behavior of (Meth)acrylate Ionomers Crosslinked by Titanium(IV), Zirconium(IV) and Niobium(V) Ions
- 細胞非接着性ヒドロゲルの調整とその特性
- ポリビニルアルコール/キトサンブレンドヒドロゲルの抗菌・防カビ性
- 細胞非接着性ポリビニルアルコール系ブレンドハイドロゲルの調製とそのゲルの溶質および酸素透過性
- 透明なポリビニルアルコールハイドロゲル膜の酸素透過性
- ポリブチレンテレフタレ-ト/ポリビスフェノ-ルAカ-ボネ-トブレンドの高速溶融紡糸線上での配向結晶化とネック状変形
- Introduction of Ag and Ag_2S Nanoparticles into Nylon 6 Film and Fiber
- Structures and Physical Properties of Cross-Linked Gelatin Fibers
- Catastrophic Neck-Flow Transition during Laser-Heated Drawing of Poly (ethylene terephthalate) Fiber
- Preparation and Optical Absorption Property of Poly(acrylic acid)/Copper Sulfide Nanocomposite Films
- Molecular Weight Dependence of Tensile Properties in Poly (vinyl alcohol) Fibers
- Preparation and Viscoelastic Behavior of Methacrylate Ionomers Crosslinked by Titanium(IV)and Zirconium(IV)
- Tensile Properties of Wet Cellulose
- Mechanical and Thermal Properties of Compression Molded Poly (acrylic acid) Salts with Multivalent Metal Ions
- Fabrication of silver plated nylon 6 nanofibers using iodine
- レーザー加熱延伸したPVDFモノフィラメントの構造と力学的性質
- Structures and Physical Properties of Cross-Linked Sericin Membranes
- ポリL-乳酸の固有複屈折度
- ゲル紡糸によるポリビニルアルコール/セリシン系ブレンド繊維の作製, 及び構造と物性
- ポリビニルアルコール/セリシン系ブレンド含水ゲル膜の構造と物性
- 反復凍結解凍ポリビニルアルコール含水ゲル中の水の状態と微細構造
- Moisture Characteristic and Structure of High Molecular Weight Sericin Film
- Structures and Physical Properties of Poly (vinyl alcohol) : Sericin Blended Plastic
- 荷電膜を通してのbi-ionic potentialの塩濃度依存性〔英文〕
- In situ study of fiber structure development of poly(butylene terephthalate) in a continuous laser-heated drawing process
- Structure and Mechanical Properties of Poly(trimethylene terephthalate) Fibers Obtained by CO_2 Laser Drawing and a Secondary Contact Heater Drawing