酸化物分散強化白金合金の高温疲労破壊
スポンサーリンク
概要
- 論文の詳細を見る
High temperature fatigue of oxide-dispersion-strengthened (ODS) platinum alloys was investigated at 1673 K and 1473 K in air. ODS platinum alloys used in this study were composed of sintered Pt-10 mass% Rh (Pt-10%Rh) alloy matrix and dispersed zirconia particles. Fatigue tests were conducted in the tension-tension cyclic mode with the R-ratio value of 0.1. Fatigue fracture surface of the ODS alloys showed clear difference from those of conventional Pt-10%Rh alloys. The fatigue strength of the ODS alloys at high temperatures were about three times higher than that of the Pt-10%Rh alloys. The fatigue rupture time of the ODS alloys was comparable to creep rupture time under a condition of maximal stress, while the fatigue rupture time of Pt-10Rh alloys is comparable to creep rupture time under a condition of average stress.
- 九州大学大学院総合理工学府の論文
- 2009-03-00
九州大学大学院総合理工学府 | 論文
- DNLS方程式を用いた平行伝播アルフヴェン波動乱流の非線形発展
- Laser Thomson Scattering and Optical Emission Studies of PDP Micro-Discharge Plasmas
- Investigation of 915 MHz ECR Plasma Parameters with SiH4/H2 Mixtures
- 日本沿岸域におけるM2潮汐振幅の季節変動および経年変動
- Silicon Dioxide Film Deposition by Afterglow-Plasma-Enhanced Chemical Vapor Deposition using Triethoxysilane and Tetraethoxysilane