高炭素鋼の炭化物亀裂による欠陥について (I)
スポンサーリンク
概要
- 論文の詳細を見る
This investigation deals with the causes of cavities which are occasionally observed at the centre of the rolled high-carbon bearing steel. Conclusions are as follows : (1) When some pressed or hammered billets are cooled down, very fine cracks, the width of which are less than 1/10μ, are formed in Acm cementite. These "Acm cementite cracks" are considered to be caused by the super-saturated hydrogen contained in the billets (hydrogen content are above 3.0cc/100) at the temp of below 200℃. (2) These "Acm cementite cracks" grow to cavities during rolling process. (3) These "Acm cementite cracks" can be observed in the form of macro-hair-cracks by etching of HCl, but cannot be observed by etching of oxidizing solutions like HNO_3 and ammonium persulphate. (4) These "Acm cementite cracks" cannot be observed in the form of flakes on fractured surface as far as the billets are simply cooled down.
- 社団法人日本鉄鋼協会の論文
- 1956-12-01
著者
関連論文
- 高炭素鋼の炭化物亀裂による欠陥について (III)
- 12 高炭素鋼の炭化物亀裂について(第 52 回講演大会講演大要)
- わが国の軸受鋼の進歩発展について
- 高炭素鋼の炭化物亀裂による欠陥について (II)
- 高炭素鋼の炭化物亀裂による欠陥について (I)
- 垂直型連続鋳造法による軸受鋼の製造
- 最近特に感じたこと
- 軸受鋼の今昔
- 56 キルド鋼々塊割れの研究(II) : 主として横割れに関する考察(製銑および製鋼, 第 55 回講演大会講演大要)
- 55 キルド鋼々塊割れの研究(I) : 主として縦割れについて(製銑および製鋼, 第 55 回講演大会講演大要)
- 18 高炭素鋼の Acm 炭化物の微少毛割れについて(第 51 回講演大会講演大要)
- 68 軸受鋼壓壊値の 2, 3 の傾向について(日本鐵鋼協會第 44 回講演大會講演大要)