高炭素鋼の炭化物亀裂による欠陥について (II)
スポンサーリンク
概要
- 論文の詳細を見る
The effects of the addition of hydrogen to 1.4% C file steel ; 1.0% C, 1.4% Cr bearing steel ; 1.0% C, Cr-W tool steel are investigated. Samples are taken from the outer side of the billets which have been confirmed that any "Acm cementite cracks" were not existed. The followings are conclusions. (1) "Acm cementite cracks" are generated in hyper-eutectoid steels by the addition of hydrogen, and the fact has been proved that the main cause of the formation of "Acm cementite cracks" was the existence of super-saturated hydrogen in the steel. (2) It has also been proved that so-called macro hair-cracks and flakes on fractured surface were only another apperances of "Acm cementite cracks" (3) The characteristic features of flakes occurence on hyper-eutectoid steel, which have not been able to explain by the use of theories about the flakes occurence on hypoeutectoid steel, can easily be understood by considering the existence of "Acm cementite cracks.
- 社団法人日本鉄鋼協会の論文
- 1957-01-01
著者
関連論文
- 高炭素鋼の炭化物亀裂による欠陥について (III)
- 12 高炭素鋼の炭化物亀裂について(第 52 回講演大会講演大要)
- わが国の軸受鋼の進歩発展について
- 高炭素鋼の炭化物亀裂による欠陥について (II)
- 高炭素鋼の炭化物亀裂による欠陥について (I)
- 垂直型連続鋳造法による軸受鋼の製造
- 最近特に感じたこと
- 軸受鋼の今昔
- 56 キルド鋼々塊割れの研究(II) : 主として横割れに関する考察(製銑および製鋼, 第 55 回講演大会講演大要)
- 55 キルド鋼々塊割れの研究(I) : 主として縦割れについて(製銑および製鋼, 第 55 回講演大会講演大要)
- 18 高炭素鋼の Acm 炭化物の微少毛割れについて(第 51 回講演大会講演大要)
- 68 軸受鋼壓壊値の 2, 3 の傾向について(日本鐵鋼協會第 44 回講演大會講演大要)