Y・Ba・Cu・O系超伝導体におけるCu-Nb置換と転移温度Tcの向上への試み

スポンサーリンク

概要

• 論文の詳細を見る

• Samples of YBa_2(Cu, Nb)_3O_y oxide were synthesized by a DC magnetronsputtering method using a YBa_2Cu_3O_y oxide as the substrate and a Nb sheet as the target. The effect of substituting Cu by Nb was studied. Diamagnetic signals of samples measured by AC susceptibility, method were detected at the temperature range of 80~86 K. Superconducting critical temperature Tc, was obtained at 93 K higher than that of the substrate of YBa_2Cu_3O_y oxides, after heat treatment at various temperatures. Some resistance anomalies that suggest a possibility of the oxide superconductor with high Tc, were observed at the temperature range of 278~284 K.

• 鹿児島大学,カゴシマ ダイガク,Kagoshima Universityの論文

著者

• 肥後 悟

  元鹿児島大学機器分析センター

関連論文

• p-Se/n-CdSeヘテロ接合のBARRIER PIEZO-EFFECT
• レーザー微細加工により作製したNBCO薄膜マイクロブリッジ接合の特性
• Y・Ba・Cu・O系超伝導体におけるCu-Nb置換と転移温度Tcの向上への試み
• Nd系およびBi系高温超伝導薄膜のエピタキシャル成膜と微細加工に関する研究(学位論文の要旨)
• 分子線エピタキシ-によるZnSe--Al薄膜の成長
• よう素を用いた化学輸送反応法によるZnS結晶およびZnS0.5Se0.5混晶のフォトルミネセンス-2-
• ヨウ素を用いた化学輸送反応法によるZnSe結晶のフォトルミネセンス-1-
• Se整流板のBARRIER PIEZO-EFFECTに関する実験-1-

スポンサーリンク