Mechanical Properties of Thin Al Wires Prepared by Electromigration
スポンサーリンク
概要
- 論文の詳細を見る
Thin Al wires with diameters of 1 to 2 μm were fabricated by electromigration by applying a current in high density to a polycrystalline Al line containing a gap and a small hole in the oxide layer used to coat the line. The fabricated Al wires were subjected to small-span bending tests under observation with a microscope, and Young's modulus and yield stress of the wire were successfully determined. The value of Young's modulus of the thin Al wire was close to that of bulk Al. On the other hand, the yield stress of the Al wire was 20 times larger than that of bulk Al. The results of structural and elemental analyses of the wire showed that pure, single-crystalline Al was obtained by electromigration. Recrystallization during wire growth might be the mechanism through which this unique crystalline structure was obtained.
- 2012-09-15
著者
-
Tohmyoh Hironori
Department Of Mechanical Engineering Tohoku University
-
Akanda Md.
Department of Mechanical Engineering, Bangladesh University of Engineering and Technology, Dhaka 1000, Bangladesh
-
Tohmyoh Hironori
Department of Nanomechanics, Tohoku University, Sendai 980-8579, Japan
-
NOBE Yuki
Department of Nanomechanics, Tohoku University, Sendai 980-8579, Japan
関連論文
- Checking Surface Contamination and Determination of Electrical Resistivity of Oxide Scale Deposited on Low Carbon Steel by DC Potential Drop Method
- Measurement of Potential Drop Distribution by Scanning the Closely Coupled Probes Sensor for Sensitive NDE of Shallow Surface Cracks
- Effective Transmission of High Frequency Ultrasound into a Silicon Chip through a Polymer Layer(Advanced Technology of Experimental Mechanics)
- Determination of Friction Coefficient of a Press-Fit Pin in Thin Plating(Macro-, Micro-, Meso-, and Nano-scopic Strength of Materials Relating to Microstructures)
- Mechanical Properties of Thin Al Wires Prepared by Electromigration
- Welding Thin Pt Wires with Dissimilar Diameters by Joule Heating
- Evaluation of Electrical Resistivity of Oxide Scale Formed under Different Conditions