Characterization of Internal Capacitors Based on Glass-Added Barium Titanate
スポンサーリンク
概要
- 論文の詳細を見る
Barium–calcium–aluminum–borosilicate glass is added as a sintering promoter to reduce the sintering temperature of barium titanate. The dielectric properties of the glass-added barium titanate-based internal capacitors are investigated. The dielectric constants of the composites were found to increase with sintering temperature. A capacitance of about 2.3 nF/cm2 with the dissipation factor of 2.9% is obtained for a 20 wt% glass-added BaTiO3 internal capacitor after being cofired with low dielectric constant ceramic substrate at 950°C. The percent change of capacitance is confined within $\pm$10% and the dissipation factor is stable in the measured temperature range.
- Publication Office, Japanese Journal of Applied Physics, Faculty of Science, University of Tokyoの論文
- 2001-07-15
著者
-
Lin Wen-kuan
Department Of Electronic Engineering I-shou University
-
Fu Shen-li
Department Of Electrical Engineering National Cheng Kung University
-
Chen Lih-shan
Department Of Electrical Engineering National Cheng Kung University
-
Huang Kwan-dar
Department Of Electronic Engineering I-shou University
-
Fu Shen-Li
Department of Electronic Engineering, I-Shou University, Kaohsiung County, Taiwan, Republic of China
-
Huang Kwan-Dar
Department of Electronic Engineering, I-Shou University, Kaohsiung County, Taiwan, Republic of China
関連論文
- Densification and Dielectric Properties of Cordierite-Lead Borosilicate Glasses
- Cosintering of Ni-Zn-Cu Ferrite with Low-Temperature Cofired Ceramic Substrates
- Dielectrie Properties of Internal Capacitors in Co-fired Ceramic Substrates
- Barium Titanate-Based Capacitors Buried into Ceramic Substrates
- Electrical Properties Of Al_2O_3- and MnO_2-Doped Thick Film Resistors on AlN Substrates
- Low Temperature Sintering of P_2O_5-Added Cordierite Glass with Borosilicate Glass
- Ultraviolet-Patternable Polymer Insulator for Organic Thin-Film Transistors on Flexible Substrates
- The Core-Shell Grain Resistance in the Reduced La-Doped (Ba, Sr)TiO_3 Ceramics
- Low-Temperature Sintering of Microwave Dielectrics (Zn,Mg)TiO3
- Multilayer Stepped-Impedance Resonator Band-Pass Filter Implementing Using Low Temperature Cofired Ceramic Structure
- Characterization of Embedded Spiral Inductors in Co-Fired Ceramic Substrates
- Characterization of Internal Capacitors Based on Glass-Added Barium Titanate