Improvement of Corrosion Resistance in Austenitic Stainless Steel by Grain Boundary Character Distribution Control
スポンサーリンク
概要
- 論文の詳細を見る
Strauss test, Coriou test and Huey test were conducted on a Type 316L austenitic stainless steel. Improvement in grain boundary corrosion resistance was verified after raising low Σ coincidence site lattice (CSL) grain boundary (GB) frequency by controlling grain boundary character distribution (GBCD). During crevice corrosion test under gamma-ray irradiation, initiation frequency of GB corrosion after GBCD controlled specimens decreased to 1/10 of GBCD uncontrolled counterpart along with lower depth of corrosion. Stress corrosion cracking (SCC) propagation rate of GBCD controlled specimen decreased to less than 1/2 of GBCD uncontrolled specimen in high temperature and high pressure water. Based on these results, we expect that GBCD control will improve corrosion resistance of austenitic material in a wide range of application and environment.
- 公益社団法人 腐食防食学会の論文
公益社団法人 腐食防食学会 | 論文
- 圧力平衡型外部照合電極による高温水溶液中の電位測定と熱拡散電位の評価
- アコースティック・エミッション（ＡＥ）による埋設鋼管の土壌腐食診断
- 光ファイバAE計測システムを用いたCBB試験中に発生する応力腐食割れの検出
- 山間部橋梁桁各部位の実測結露時間によるぬれ環境評価
- 火力発電プラントにおけるサイクル化学の最近の話題