Corrosion Behavior of AZ31 Magnesium Alloy in Dilute Sodium Chloride Solutions
スポンサーリンク
概要
- 論文の詳細を見る
Corrosion behavior of AZ31 magnesium alloy in dilute NaCl solutions was studied by electrochemical techniques. Its surface film was chemically characterized by X-ray diffraction (XRD). A corrosion map in terms of electrode potential and chloride concentration [Cl–] was obtained by using electrochemical measurements. With the map, passivation and corrosion zones were determined. The passivation zone was found to become narrow with the increasing of [Cl–] . The values of Eocp, open-circuit potential, in nondeaerated NaCl solutions were in the passivation zone when [Cl–] <0.2 M and in the corrosion zone when [Cl–] ≥0.2 M. The reduction reactions of dissolved oxygen and hydrogen evolution worked as cathodic reactions in nondeaerated solutions. By XRD analyses, Mg(OH)2, magnesium hydroxyl carbonate, and MgO were the dominant products in the corrosion zone, whereas magnesium hydroxyl carbonate and MgO were the main components in the passivated film.
- 公益社団法人 腐食防食学会の論文
公益社団法人 腐食防食学会 | 論文
- 圧力平衡型外部照合電極による高温水溶液中の電位測定と熱拡散電位の評価
- アコースティック・エミッション（ＡＥ）による埋設鋼管の土壌腐食診断
- 光ファイバAE計測システムを用いたCBB試験中に発生する応力腐食割れの検出
- 山間部橋梁桁各部位の実測結露時間によるぬれ環境評価
- 火力発電プラントにおけるサイクル化学の最近の話題