Development of a Radio-frequency Air-injection Press for Manufacturing Particleboard from High-moisture Raw Particles I.:Effects of the radio-frequency air-injection press on properties of particleboards
スポンサーリンク
概要
- 論文の詳細を見る
Particleboards were manufactured from high-moisture raw particles using a radio-frequency press which has both hot-press heating and radio-frequency heating, and the properties of the boards were analyzed. The pressing time was at least 8 min and the internal bond strength was 0.192 MPa when the boards were manufactured using only hot press heating without radio-frequency heating. However, a reduction in pressing time to just 3 min and an increase in internal bond strength to 0.440 MPa was possible when the board was manufactured using the radio-frequency press. Using the radio-frequency press caused the temperature of the inside of the boards to rise sharply and this resulted in a great reduction in pressing time and an increase in internal bond strength. Moreover, the pressing time was reduced to 2.5 min and the internal bond strength was increased to 0.552 MPa by installing an air-injection device on the radio-frequency press. Further reduction of pressing time and increase in internal bond strength were achieved by air injection. As a result, it was clarified that the internal bond strength of the boards could be achieved even when the binder resin content was reduced by approximately 25%.
- The Japan Wood Research Societyの論文
The Japan Wood Research Society | 論文
- 静的曲げモーメントを受けるタケ・ヒノキ接着板の応力と強度
- アラゲキクラゲ(Auricularia polytricha)培地の炭水化物含有量と子実体発生量の相関
- 樹皮タンニンの化学特性と化学・酵素変換
- ヤシ殻チャーからのKOH-水蒸気二段階賦活炭の製造とその吸着特性
- 木造住宅の構造部材に生じる各種応力の許容応力度に対する割合(第5報) 一般地域に建設された住宅の梁に強度等級E55-F200の構造用集成材を使用した場合:一般地域に建設された住宅の梁に強度等級E55-F200の構造用集成材を使用した場合