The nanostructure of MgO-templated carbon synthesized through the decomposition of magnesium citrate was examined, and its structural change induced by heat-treatment was traced using various analysis techniques. A high resolution TEM analysis revealed that the carbon consisted of hollow nanoparticles with a size of 10 nm where the thickness of the carbon walls (shells) is several nanometers. N2 adsorption analysis indicated that the MgO-templated carbon before the heat-treatment was highly mesoporous and microporous with a BET specific surface area as large as 1600 m2/g. Such a porous structure was almost unchanged even for the carbon heat-treated at 2000 °C, although surface areas of activated carbons were usually decreased in the lower temperature ranges. Above 2000 °C, the carbon nanostructure observed by TEM changed so that it was similar to heat-treated glassy carbon which is normally non-graphitizable. The templated-carbon, however, was graphitized by multiphase graphitization process with three different (004) diffraction peaks of carbon. The reason why such inconsistency occurred was not clear, but could be because of the difference in the surface area which is negligible for glassy carbons but not for the MgO-templated carbon.
著者
関連論文
- MgO鋳型カーボンの細孔構造と応用
- セラミックスのカーボン被覆
- クエン酸マグネシウムとポリビニルアルコール混合物からのメソポーラスカーボンの調製
- 熱可塑性樹脂とマグネシウム塩混合物からの賦活処理を経ないメソポーラスカーボンの調製
- 熱可塑性炭素前駆体/MgO混合物の炭素化による多孔質炭素の調製
- MgO鋳型メソポーラス炭素のナノ構造とその熱処理に伴う変化
- MgO鋳型メソポーラス炭素のナノ構造とその熱処理に伴う変化
- MgO鋳型メソポーラス炭素のナノ構造とその熱処理に伴う変化
- Performance of MgO-templated mesoporous carbons as electrode materials in lithium-ion capacitor
- MgO鋳型メソポーラス炭素のリチウムイオンキャパシタ特性