電位ノイズ法で推定した準安定食孔深さの極値分布

概要

論文の詳細を見る
The extreme-value distribution of metastable-pit depths on SUS304 stainless-steel electrodes was examined. The electrode with the surface area of 10mm<SUP>2</SUP> was immersed in a 10mass% NaCl solution at 60, 70 or 80°C, and measured its potential noises for 48hours. The depth of the metastable pits was calculated from the electric quantity of the local anodic currents that were estimated from the measured potential noises by using the RPS method, assuming the shape of the metastable pits as true hemispheres. The maximum pit depths for 7 to 8 samples at 70 and 80°C were fairly approximated to a Gumbel distribution. The minimum surface area required for forming the stable pit was estimated about 10000mm<SUP>2</SUP>, under the conditions employed in this study. From the return period equivalent to this surface area, the critical pit depths at 70 and 80°C were estimated 6.4 and 9.4μm, respectively.