Crack propagation tests on a bulk metallic glass, Zr<SUB>55</SUB>Cu<SUB>30</SUB>Ni<SUB>5</SUB>Al<SUB>10</SUB>, were conducted either in aqueous sodium chloride (NaCl) solutions or high purity water under sinusoidal cyclic loading or sustained loading. Although the crack growth rate in high purity water was almost identical to that in air, the rate in NaCl solution was much higher than that in air even in a very low concentration of NaCl such as 0.01%. In 3.5% NaCl solution, the time-based crack propagation rate during cyclic loading, d<I>a</I>/d<I>t</I>, was determined by the maximum stress intensity factor, <I>K</I><SUB>max</SUB>, but was almost independent of the loading frequency and the stress ratio, and the rate was close to that of environment-assisted cracking under a sustained load.
著者
関連論文
- 高温超伝導SQUID顕微鏡を用いたプリント配線の欠陥検出
- 高輝度放射光CT法による腐食疲労損傷の観察
- OS0602 リアルサイズのモデルコンポジットを用いたモードII繊維/樹脂界面はく離靱性の評価(先進複合材料の強度・特性評価,オーガナイズドセッション)
- Zr基バルク金属ガラス切欠き材の疲労強度
- OS0724 オーステナイト系ステンレス鋼の疲労損傷によるマルテンサイト変態挙動の観察(構造用材料の疲労挙動と寿命評価,オーガナイズドセッション)
- 二種類のリアルサイズモデル複合材料を用いたFRP中のモードI繊維／樹脂界面破壊靭性と樹脂靭性の分離評価
- 1508 光造形法により作製したCNT/紫外線硬化樹脂複合材料マイクロエレメントの引張試験(OS15-2 ナノ・マイクロの視点からの変形と破壊の力学)
- 1507 マイクロモデルコンポジットによるモードI繊維/樹脂界面破壊靭性の評価および樹脂靭性評価への適用(OS15-2 ナノ・マイクロの視点からの変形と破壊の力学)
- Effect of Hydrogen Absorption in TiNi Shape-Memory Alloy Thin Wire on SSRT Strength
- 繊維２本および繊維４本のモデル複合材料を用いた繊維／樹脂界面はく離じん性の実験的評価とＦＲＰじん性への寄与の検討
- ３次元編み構造からなる生分解性複合材料スカフォールドの力学的特性と生分解性特性の評価
- リアルサイズのモデル複合材料を用いたモードＩ繊維／樹脂界面破壊じん性の評価
- Effect of Yield Phenomenon on Fatigue Damage in Commercially Pure Iron Thin Wires
- 放射光マイクロトモグラフィによる鋼中のき裂観察
- Ｚｒ基バルク金属ガラスの環境助長き裂伝ぱ
- Effect of Hydrogen Absorption on Mechanical Properties of TiNi Shape Memory Alloy Thin Wire
- OS0513 SUS304鋼の応力誘起マルテンサイト変態を利用した疲労損傷評価(OS5-3 疲労損傷,OS-5 材料の疲労挙動と損傷評価1)